纳米b-Ni(OH)<sub>2</sub>的制备及其储锂性能

李延伟; 潘观林; 姚金环; 李世玉; 张灵志

doi:10.11949/j.issn.0438-1157.20150624

您当前的位置：

首页 >

文章列表页 >

纳米b-Ni(OH)₂的制备及其储锂性能

能源和环境工程 | 更新时间：2025-12-10

- 纳米b-Ni(OH)₂的制备及其储锂性能
- Preparation and lithium ion storage performance of nano-sized β-Ni(OH)₂
- 化工学报 2015年第12期页码：5088-5095
- 作者机构：
  
  1. 桂林理工大学化学与生物工程学院, 广西电磁化学功能物质重点实验室,广西,桂林,541004
  2. 中国科学院可再生能源重点实验室,广东,广州,510640
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150624
  中图分类号： Q152
- 网络首发：2015-12-05，
  
  纸质出版：2015-12-05
- 稿件说明：
移动端阅览
李延伟, 潘观林, 姚金环, 等. 纳米b-Ni(OH)₂的制备及其储锂性能[J]. 化工学报, 2015,(12):5088-5095. DOI: 10.11949/j.issn.0438-1157.20150624.

LI Yanwei, PAN Guanlin, YAO Jinhuan, et al. Preparation and lithium ion storage performance of nano-sized β-Ni(OH)₂[J]. CIESC Journal, 2015, (12): 5088-5095. DOI: 10.11949/j.issn.0438-1157.20150624.
李延伟, 潘观林, 姚金环, 等. 纳米b-Ni(OH)₂的制备及其储锂性能[J]. 化工学报, 2015,(12):5088-5095. DOI: 10.11949/j.issn.0438-1157.20150624. DOI：

LI Yanwei, PAN Guanlin, YAO Jinhuan, et al. Preparation and lithium ion storage performance of nano-sized β-Ni(OH)₂[J]. CIESC Journal, 2015, (12): 5088-5095. DOI: 10.11949/j.issn.0438-1157.20150624. DOI：

摘要

以Ni(NO3)2·6H2O和NaOH为原料采用化学沉淀法制备了Ni(OH)2电极材料。采用X射线衍射(XRD)和场发射扫描电子显微镜(FESEM)表征了样品的微观结构

结果表明该样品是具有片状纳米次级结构的β-Ni(OH)2。采用循环伏安(CV)和电化学充放电测试研究了该β-Ni(OH)2样品的储锂性能

结果发现该样品作为锂离子电池负极材料具有非常高的储锂活性

在50 mA·g-1电流密度下其第3次循环放电比容量高于1550 mA·h·g-1;样品电极中的碳含量对其循环性能和倍率性都有显著影响

通过交流阻抗(EIS)测试分析了样品电极中碳含量的作用机理。

Abstract

Ni(OH)2 sample is prepared by chemical precipitation method with Ni(NO3)2·6H2O and NaOH as raw materials. X-ray diffraction (XRD) and field emission scanning electron microscope (FESEM) analysis reveal that the sample is β-Ni(OH)2 with sheet-like hierarchical nanostructure. Cyclic voltammograms (CV) and charge-discharge tests are performed to study the lithium ion storage performance of the β-Ni(OH)2 sample. The results show that the prepared β-Ni(OH)2 sample has a very high lithium ion storage activity. For example

at a charge-discharge current density of 50 mA·g-1

the discharge capacity of the third cycle for the prepared β-Ni(OH)2 is higher than 1550 mA·h·g-1. The carbon content in electrode has a great influence on both the cyclic stability and rate performance of the β-Ni(OH)2 sample. The mechanism of carbon content on lithium storage performance of the β-Ni(OH)2 sample is analyzed by electrochemical impedance spectroscopy (EIS) tests.

关键词

Keywords

references

浏览量

242

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

具有优异锂存储性能的蛋黄蛋壳结构FeS2@CFs薄膜电极

核壳结构米粒状FeS2/C纳米材料制备及储锂性能研究

Mo2N量子点@N-掺杂石墨烯复合材料的制备及储锂性能

纳米多孔NiO类空心微球负极材料的制备与储锂性能

基于递归特性和CNN的上升管内气液两相流型识别研究

纳米b-Ni(OH)2的制备及其储锂性能

Preparation and lithium ion storage performance of nano-sized β-Ni(OH)2

DOI：10.11949/j.issn.0438-1157.20150624

摘要

Abstract

关键词

Keywords

references

纳米b-Ni(OH)₂的制备及其储锂性能

Preparation and lithium ion storage performance of nano-sized β-Ni(OH)₂