水相添加剂对热可膨胀聚合物微球颗粒结构和膨胀特性的影响

谢贵明; 王稚阳; 包永忠

doi:10.11949/j.issn.0438-1157.20150489

您当前的位置：

首页 >

文章列表页 >

水相添加剂对热可膨胀聚合物微球颗粒结构和膨胀特性的影响

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 水相添加剂对热可膨胀聚合物微球颗粒结构和膨胀特性的影响
- Effect of water phase additives on particle structure and expansion behavior of thermal-expandable polymer microspheres
- 化工学报 2015年第11期页码：4682-4688
- 作者机构：
  
  1. 浙江大学化学工程与生物工程学院, 化学工程联合国家重点实验室(浙江大学),浙江,杭州,310027
  2. 贵州大学化学与化工学院,贵州,贵阳,550025
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150489
  中图分类号： Q325
- 网络首发：2015-11-05，
  
  纸质出版：2015-11-05
- 稿件说明：
移动端阅览
谢贵明, 王稚阳, 包永忠. 水相添加剂对热可膨胀聚合物微球颗粒结构和膨胀特性的影响[J]. 化工学报, 2015,(11):4682-4688.

XIE Guiming, WANG Zhiyang, BAO Yongzhong. Effect of water phase additives on particle structure and expansion behavior of thermal-expandable polymer microspheres[J]. CIESC Journal, 2015, (11): 4682-4688.
谢贵明, 王稚阳, 包永忠. 水相添加剂对热可膨胀聚合物微球颗粒结构和膨胀特性的影响[J]. 化工学报, 2015,(11):4682-4688. DOI： 10.11949/j.issn.0438-1157.20150489.

XIE Guiming, WANG Zhiyang, BAO Yongzhong. Effect of water phase additives on particle structure and expansion behavior of thermal-expandable polymer microspheres[J]. CIESC Journal, 2015, (11): 4682-4688. DOI： 10.11949/j.issn.0438-1157.20150489.

摘要

通过戊烷发泡剂存在下的偏氯乙烯-丙烯腈-甲基丙烯酸甲酯(VDC-AN-MMA)悬浮共聚制备包覆型热可膨胀聚合物微球

考察氯化钠、柠檬酸和重铬酸钾等水相添加剂对聚合物微球颗粒结构和热膨胀特性的影响。结果表明氯化钠、柠檬酸和重铬酸钾的添加均可起到降低聚合过程中形成难膨胀聚合物细微粒子的作用

当氯化钠添加量为4%(质量分数

基于单体

下同)、柠檬酸添加量为2.5%～5.0%、重铬酸钾添加量为0.05%～0.1%时

制备的可膨胀聚合物微球具有粒径分布窄、形态规整、聚合物对发泡剂包覆效果好等特点;加热后未膨胀聚合物微粒数目少

膨胀均匀

膨胀温度区间宽。

Abstract

Thermal-expandable polymer microspheres with core-shell structure were synthesized by suspension copolymerization of vinylidene chloride-acrylonitrile-methyl methacrylate (VDC-AN-MMA) in the presence of pentane as a foaming agent. The influence of water phase additives

such as sodium chloride

citric acid and potassium dichromate

on the particle structure and thermal expansion properties of polymer microspheres were investigated. The results showed that the additions of sodium chloride

citric acid and potassium dichromate could significantly reduce the number of un-expandable fine polymer particles. To be specific

when the loading of sodium chloride

citric acid and potassium dichromate was 4%

2.5%—5.0% and 0.05%—0.1% (based on monomers)

respectively

the prepared expandable microspheres exhibited narrow particle size distributions

regular morphology and good encapsulation of foaming agent by polymer. Few particles were unexpanded and the expansion of particles was uniform after the heat treating of the microspheres.

关键词

Keywords

references

浏览量

871

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

数字全息在线测量煤粉粒度分布

机器学习在结晶过程建模与控制中的研究进展

新型黏弹性颗粒驱油剂耐温抗盐机理研究

基于预辐射接枝法的DMAPS改性PVDF超亲水膜的制备及其油/水乳液分离性能

非均相茂金属催化剂载体研究进展