侧氨基聚硅氧烷改性聚氨酯涂层剂的制备与性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 侧氨基聚硅氧烷改性聚氨酯涂层剂的制备与性能
- Synthesis and characterization of side aminopolysiloxane modifiedpolyurethane textile coatings
- 化工学报 2015年第11期页码：4710-4715
- 作者机构：
  
  1. 潍坊科技学院山东半岛蓝色经济工程研究院,山东,潍坊,262700
  2. 北京理工大学材料科学与工程学院,北京,100081
  3. 中国科学院高能物理研究所, 核分析技术重点实验室,北京,100049
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150421
  中图分类号： Q314.2
- 网络首发：2015-11-05，
  
  纸质出版：2015-11-05
- 稿件说明：
移动端阅览
雷海波, 罗运军, 冯丽娟, 等. 侧氨基聚硅氧烷改性聚氨酯涂层剂的制备与性能[J]. 化工学报, 2015,(11):4710-4715.

LEI Haibo, LUO Yunjun, FENG Lijuan, et al. Synthesis and characterization of side aminopolysiloxane modifiedpolyurethane textile coatings[J]. CIESC Journal, 2015, (11): 4710-4715.
雷海波, 罗运军, 冯丽娟, 等. 侧氨基聚硅氧烷改性聚氨酯涂层剂的制备与性能[J]. 化工学报, 2015,(11):4710-4715. DOI： 10.11949/j.issn.0438-1157.20150421.

LEI Haibo, LUO Yunjun, FENG Lijuan, et al. Synthesis and characterization of side aminopolysiloxane modifiedpolyurethane textile coatings[J]. CIESC Journal, 2015, (11): 4710-4715. DOI： 10.11949/j.issn.0438-1157.20150421.

摘要

以侧氨基聚硅氧烷(SAPDMS)、聚四氢呋喃醚、聚乙二醇为混合软段

二羟甲基丙酸为亲水扩连剂

4-丁二醇为硬段调节剂

与异佛尔酮二异氰酸酯反应合成了水性有机硅改性聚氨酯(WSSPU)

并以WSSPU为基础制备了防水透湿织物涂层剂。分别采用红外光谱、差热扫描量热仪、动态力学分析仪、正电子湮灭寿命谱等表征了WSSPU膜的组成与微观结构

考察了WSSPU膜的力学性能和涂层织物的防水透湿性能。结果表明

当侧氨基聚硅氧烷用量(质量比)< 15%时

可以制得稳定的乳液。聚硅氧烷改性后膜内部微相分离结构更加明显

自由体积空洞变大

透湿性能提高。

Abstract

The water-borne side aminopolysiloxane modified polyurethanes (WSSPU) were prepared by polyaddition reaction using poly(tetramethylene oxide)glycol

polyethylene glycol

and side aminopolysiloxane as soft segments

dimethylolpropionic acid as hydrophilic chain extender

4-butanediol as hard segment regulator and isophorone diisocyanate. The waterproof and moisture permeable textile coating agent was then fabricated based on WSSPU. The chemical composition and microstructure of WSSPU were characterized by infrared spectroscopy

differential scanning calorimetry

dynamic mechanical analyzer and positron annihilation lifetime spectroscopy

respectively. The mechanical properties of WSSPU films

the waterproofness and breathability of the coated fabric were determined. The results showed that the stable emulsion can be obtained at the amount of SAPDMS (mass ratio) below 15%. The modified polyurethane membranes had more serious micro-phase separation structure and increased free hole volume

resulting in improved moisture permeability.

关键词

Keywords

references

浏览量

254

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

聚氨酯改性沥青高低温性能及影响因素的研究进展

水性聚氨酯基氧化铟锡蚀刻油墨的制备与性能

羧酸盐/磺酸盐复合型WPU胶黏剂的制备与表征

新型TMPPs/非离子型水性聚氨酯的合成与性能

部分预混旋流燃烧入口激励下的熵波产生及耗散机制研究