P123对聚醚砜纳米纤维膜结构和性能的影响

材料化学工程与纳米技术 | 更新时间：2025-12-10

- P123对聚醚砜纳米纤维膜结构和性能的影响
- Effect of P123 on structures and properties of PES nanofibrous membranes
- 化工学报 2015年第11期页码：4676-4681
- 作者机构：
  
  华东理工大学化学工程联合国家重点实验室, 上海市多相结构材料化学工程重点实验室, 化学工程研究所膜科学与工程研发中心,上海,200237
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150419
  中图分类号： Q31
- 网络首发：2015-11-05，
  
  纸质出版：2015-11-05
- 稿件说明：
移动端阅览
马晓华, 许振良. P123对聚醚砜纳米纤维膜结构和性能的影响[J]. 化工学报, 2015,(11):4676-4681.

MA Xiaohua, XU Zhenliang. Effect of P123 on structures and properties of PES nanofibrous membranes[J]. CIESC Journal, 2015, (11): 4676-4681.
马晓华, 许振良. P123对聚醚砜纳米纤维膜结构和性能的影响[J]. 化工学报, 2015,(11):4676-4681. DOI： 10.11949/j.issn.0438-1157.20150419.

MA Xiaohua, XU Zhenliang. Effect of P123 on structures and properties of PES nanofibrous membranes[J]. CIESC Journal, 2015, (11): 4676-4681. DOI： 10.11949/j.issn.0438-1157.20150419.

摘要

通过静电纺丝法制备了聚醚砜(PES)/聚环氧乙烷-聚环氧丙烷-聚环氧乙烷三嵌段共聚物(P123

PEO20PPO70PEO20

Ma=5800)纳米纤维膜

考察了P123含量对纺丝液的黏度和表面张力的影响

以及对所制备的纳米纤维膜的结构和性能的影响。实验结果表明:P123含量从3%(质量)增至9%时

其纺丝液的黏度由300 mPa·s增至1000 mPa·s

表面张力在36.5～37.8 mN·m-1范围内;P123改性的PES纳米纤维直径约为360 nm

分布均匀

其表面也比较光滑

取向趋于一致;此外

该纳米纤维膜具有良好的机械性能和耐溶胀性能

较大的比表面积(>39 m2·g-1)

孔隙率

可用作催化剂载体。

Abstract

Polyether sulfone (PES)/polyethylene oxide-polypropylene oxide-polyethylene oxide triblock copolymer (P123

PEO20PPO70PEO20

Ma 5800) nanofibrous membrane was prepared via electrospinning. The influence of P123 content on viscosity and surface tension of spinning solution was investigated as well as the effect on structures and properties of the formed nanofibrous membranes. The results showed that the viscosity and surface tension of spinning solution increased from 300 to 1000 mPa·s and 36.5 to 37.8 mN·m-1 with increasing P123 content from 3% to 9%

respectively. The diameter of the obtained PES/P123 nanofibers was about 360 nm. The formed PES/P123 nanofibrous membranes had a uniform distribution

smooth surface and good mechanical and swelling properties. They also had large specific surface area (>39 m2·g-1) and porosity

and could be used as catalyst support.

关键词

Keywords

references

浏览量

227

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

注射压缩成型聚碳酸酯制品的低温拉伸力学性能

MF-PU双壳层香精油微胶囊的制备及性能研究

富氧空位锌掺杂PdO/ZrO2催化CO2和苯酚合成碳酸二苯酯

过渡金属基氮掺杂炭的构筑及其脱硫性能研究

碱金属改性对SrMnO3催化乙苯化学链氧化脱氢性能的影响规律研究