氨基修饰复合型钠基吸收剂的脱碳特性

余帆; 吴烨; 董伟; 蔡天意; 张文静; 张聪; 陈晓平

doi:10.11949/j.issn.0438-1157.20150060

您当前的位置：

首页 >

文章列表页 >

氨基修饰复合型钠基吸收剂的脱碳特性

能源和环境工程 | 更新时间：2025-12-10

- 氨基修饰复合型钠基吸收剂的脱碳特性
- Carbonation characteristics of sodium-based sorbents with aminomodification for CO₂ capture
- 化工学报 2015年第10期页码：4218-4227
- 作者机构：
  
  1. 东南大学能源与环境学院, 能源热转换及其过程测控教育部重点实验室,江苏,南京,210096
  2. 南京理工大学能源与动力工程学院,江苏,南京,210094
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150060
  中图分类号： K09
- 网络首发：2015-10-05，
  
  纸质出版：2015-10-05
- 稿件说明：
移动端阅览
余帆, 吴烨, 董伟, 等. 氨基修饰复合型钠基吸收剂的脱碳特性[J]. 化工学报, 2015,(10):4218-4227.

YU Fan, WU Ye, DONG Wei, et al. Carbonation characteristics of sodium-based sorbents with aminomodification for CO₂ capture[J]. CIESC Journal, 2015, (10): 4218-4227. DOI: 10.11949/j.issn.0438-1157.20150060.
余帆, 吴烨, 董伟, 等. 氨基修饰复合型钠基吸收剂的脱碳特性[J]. 化工学报, 2015,(10):4218-4227. DOI： 10.11949/j.issn.0438-1157.20150060.

YU Fan, WU Ye, DONG Wei, et al. Carbonation characteristics of sodium-based sorbents with aminomodification for CO₂ capture[J]. CIESC Journal, 2015, (10): 4218-4227. DOI: 10.11949/j.issn.0438-1157.20150060. DOI：

摘要

为弥补常规钠基吸收剂活性差、脱碳量低的不足

制备了多种表面氨基修饰的新型复合型钠基吸收剂并研究其脱碳特性。通过比较氨基流失率和实际脱碳量

选定二氧化硅的前驱物正硅酸乙酯为载体前驱物

以碳酸钠为活性成分

分别以3-氨基丙基三甲氧基硅烷(APS)、3-氨基丙基三乙氧基硅烷(APTES)、二乙烯三胺(DETA)、三乙烯四胺(TETA)为氨基前驱物

制备得到多种表面氨基修饰的复合型钠基吸收剂。探究各种吸收剂的孔隙结构与脱碳特性

结果表明

APS、APTES修饰后吸收剂孔隙特性较差

脱碳量较低

DETA、TETA修饰后吸收剂孔隙结构得到改善

脱碳量较高。

Abstract

In order to improve the CO2 sorption performance of sodium-based sorbent

a series of sodium-based sorbents with amino modification were prepared by sol-gel method and the corresponding CO2 sorption capacity were investigated in this paper. Tetraethylorthosilicate (TEOS) was chosen as the carrier precursor by comparing the amine loss rate and CO2 sorption capacity of pure -NH2 sorbents

and Na2CO3 was as the active ingredient. 3-aminopropyltrimethoxysilane (APS)

3-aminopropyltriethoxysilane (APTES)

diethylenetriamine (DETA) and triethylenetetramine (TETA) were used

respectively as the amino precursor for synthesizing the composite sorbents and then drying them with conventional technique. Results showed that the sorbent modified with TETA had the highest CO2 sorption capacity and the best pore structure

while that modified with APTES had the lowest amine loss but poor structure.

关键词

Keywords

references

浏览量

200

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

N2优先渗透ZIF-8复合膜的制备及其CO2捕集

聚乙烯胺/埃洛石纳米管混合基质膜的制备及其CO2/N2分离

胺基CO2固体吸附剂脱碳特性及SO2的影响

一种低能耗捕集CO2煤基甲醇和电力联产过程设计

蒸汽活化水泥支撑钙基吸收剂活性及强度特性