新型多胺羧甲基壳聚糖的合成及对Ni(Ⅱ)的吸附特性

分离工程 | 更新时间：2025-12-10

- 新型多胺羧甲基壳聚糖的合成及对Ni(Ⅱ)的吸附特性
- Synthesis of carboxymethyl polyamines chitosan and its adsorption properties for Ni(Ⅱ)
- 化工学报 2015年第5期页码：1785-1791
- 作者机构：
  
  中南大学化学化工学院,湖南,长沙,410083
- 作者简介：
- 基金信息：
  
  国家自然科学基金项目(21006129,21276284,21146008)。
- DOI：10.11949/j.issn.0438-1157.20141197
  中图分类号： Q2TQ31
- 网络首发：2015-05-05，
  
  纸质出版：2015-05-05
- 稿件说明：
移动端阅览
桂珊, 刘贡钢, 姜珩, 等. 新型多胺羧甲基壳聚糖的合成及对Ni(Ⅱ)的吸附特性[J]. 化工学报, 2015,(5):1785-1791.

GUI Shan, LIU Gonggang, JIANG Heng, et al. Synthesis of carboxymethyl polyamines chitosan and its adsorption properties for Ni(Ⅱ)[J]. CIESC Journal, 2015, (5): 1785-1791.
桂珊, 刘贡钢, 姜珩, 等. 新型多胺羧甲基壳聚糖的合成及对Ni(Ⅱ)的吸附特性[J]. 化工学报, 2015,(5):1785-1791. DOI： 10.11949/j.issn.0438-1157.20141197.

GUI Shan, LIU Gonggang, JIANG Heng, et al. Synthesis of carboxymethyl polyamines chitosan and its adsorption properties for Ni(Ⅱ)[J]. CIESC Journal, 2015, (5): 1785-1791. DOI： 10.11949/j.issn.0438-1157.20141197.

摘要

为了提高壳聚糖(CS)吸附重金属的能力

对表面含有氨基乙酸基团的新型多胺羧甲基壳聚糖(CTGCS)进行了合成研究。其合成过程为:以CS为原料

通过戊二醛交联得到壳聚糖树脂(GCS)

再经四乙烯五胺改性

得到多胺壳聚糖树脂(TGCS)

最后采用一氯乙酸进行修饰

得到了目标产物(CTGCS)。通过对CS、GCS、TGCS和CTGCS进行红外光谱和XPS分析

对合成过程进行了分析。吸附结果表明

CTGCS对Ni2+的吸附规律符合Freundlich 等温式模型

吸附过程符合拟二级动力学模型

最大平衡吸附量为533.8 mg·g-1

比TGCS的吸附量增加了1.5倍。

Abstract

A novel amino acid functionalized polyamine carboxymethyl chitosan (CTGCS) was designed to improve adsorption ability of chitosan (CS) for heavy metals. Chitosan resin (GCS) was firstly obtained via cross-link reaction of chitosan and glutaraldehyde. After following modification by tetraethylenepentamine and chloroacetic acid

CTGCS was successfully synthesized. The samples at different reaction steps were characterized by using FTIR and XPS to understand reaction mechanism. Moreover

the adsorption ability of as-synthesized CTGCS for Ni2+ from aqueous solutions was investigated. The adsorption process conformed with the Freundlich isotherm model and could be fitted by the pseudo-second order kinetics model. The maximum adsorption capacity of CTGCS for Ni2+ was significantly improved up to 533.8 mg·g-1

about 1.5 times more than that of TGCS

indicating that CTGCS was a promising adsorbent for heavy metals.

关键词

Keywords

references

浏览量

212

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

温度敏感聚N-异丙基丙烯酰胺/谷氨酸钠/壳聚糖复合材料制备及吸附性能研究

中空孔结构对W掺杂MFI分子筛丙酮吸附行为的研究

新型壳聚糖/锆复合球的制备及硼吸附性能

乙二胺丙酰化交联壳聚糖微球对甲基橙的吸附性能

L-胱氨酸交联球形壳聚糖凝胶的制备与Cu2+吸附性能