纳/微复合结构TiO<sub>2</sub>负载催化剂的加氢脱硫性能

汪怀远; 程小双; 王池嘉; 肖博; 蒋凤

doi:10.11949/j.issn.0438-1157.20141083

您当前的位置：

首页 >

文章列表页 >

纳/微复合结构TiO₂负载催化剂的加氢脱硫性能

催化、动力学与反应器 | 更新时间：2025-12-10

- 纳/微复合结构TiO₂负载催化剂的加氢脱硫性能
- Hydrodesulfurization performance of nano/micro-composite TiO₂ supported catalysts
- 化工学报 2015年第1期页码：114-120
- 作者机构：
  
  东北石油大学化学化工学院,黑龙江,大庆,163318
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20141083
  中图分类号： 643.3
- 网络首发：2015-01-05，
  
  纸质出版：2015-01-05
- 稿件说明：
移动端阅览
汪怀远, 程小双, 王池嘉, 等. 纳/微复合结构TiO₂负载催化剂的加氢脱硫性能[J]. 化工学报, 2015,(1):114-120. DOI: 10.11949/j.issn.0438-1157.20141083.

WANG Huaiyuan, CHENG Xiaoshuang, WANG Chijia, et al. Hydrodesulfurization performance of nano/micro-composite TiO₂ supported catalysts[J]. CIESC Journal, 2015, (1): 114-120. DOI: 10.11949/j.issn.0438-1157.20141083.
汪怀远, 程小双, 王池嘉, 等. 纳/微复合结构TiO₂负载催化剂的加氢脱硫性能[J]. 化工学报, 2015,(1):114-120. DOI: 10.11949/j.issn.0438-1157.20141083. DOI：

WANG Huaiyuan, CHENG Xiaoshuang, WANG Chijia, et al. Hydrodesulfurization performance of nano/micro-composite TiO₂ supported catalysts[J]. CIESC Journal, 2015, (1): 114-120. DOI: 10.11949/j.issn.0438-1157.20141083. DOI：

摘要

以传统固相烧结法制备的不稳定的层状K2Ti2O5为前驱体

直接将钛酸钾晶须进行离子交换得到具有纳微复合结构的TiO2载体

等体积浸渍法制备出MoO3/TiO2催化剂

运用SEM、XRD、BET、TEM等技术手段对载体和催化剂进行表征

并考察了该TiO2复合结构负载催化剂的加氢脱硫催化活性。SEM和XRD分析显示:该纳微米复合结构是由纳米颗粒与微米晶须构成的特殊结构

拥有不同形貌和尺寸的TiO2却具有相同的锐钛矿相。与单独TiO2纳米粒子和TiO2晶须相比

TiO2复合结构负载催化剂表现出更佳的脱硫催化能力

在温度310℃、压力2.1 MPa、体积空速6 h-1、氢/油体积比600条件下

催化剂表现出优异的DBT脱硫性能。

Abstract

With unstable layered K2Ti2O5 as the precursor in the traditional preparation of solid phase sintering

nano/micro-composite TiO2 (TiO2-m) derived from K2Ti2O5 was synthesized via ion-exchange. Supported MoO3/TiO2-m catalysts were prepared by incipient impregnation. Simultaneously

the properties of supports and catalysts were characterized by means of SEM

XRD

BET and TEM. An investigation into the HDS performance of MoO3/TiO2-m catalysts for dibenzothiophene was performed. SEM and XRD results showed that the prepared TiO2-m supports were shaped in nano-scale particle and micron-sized whisker morphology

having the same anatase phase with different morphologies and sizes of TiO2. Compared with pure morphology control sample

HDS tests indicated that Mo catalysts supported on TiO2-m showed the best HDS catalytic activity under relatively mild reaction conditions (310℃

2.1 MPa

LHSV 6 h-1 and H2/feed ratio 600 m3·m-3).

关键词

Keywords

references

浏览量

705

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

静电纺丝法制备氧化钛-氧化石墨复合载体的加氢脱硫性能

BiOBr的形貌调控及其光催化CO2还原性能的研究

Ni/Al2O3与ZnO距离对含硫菲加氢性能的影响

Al2O3载体孔结构优化：提升FeMo/Al2O3催化剂在焦炉煤气加氢脱硫性能

原子尺度钼系加氢脱硫催化剂的研究进展与展望

纳/微复合结构TiO2负载催化剂的加氢脱硫性能

Hydrodesulfurization performance of nano/micro-composite TiO2 supported catalysts

DOI：10.11949/j.issn.0438-1157.20141083

摘要

Abstract

关键词

Keywords

references

纳/微复合结构TiO₂负载催化剂的加氢脱硫性能

Hydrodesulfurization performance of nano/micro-composite TiO₂ supported catalysts