超重力法制备La0.5Pb0.5MnO3及其在碳酸二苯酯合成中的应用

鲁超; 金放; 袁华; 杜治平; 吴元欣

您当前的位置：

首页 >

文章列表页 >

超重力法制备La_0.5Pb_0.5MnO₃及其在碳酸二苯酯合成中的应用

催化、动力学与反应器 | 更新时间：2025-12-10

- 超重力法制备La_0.5Pb_0.5MnO₃及其在碳酸二苯酯合成中的应用
- Preparation of La_0.5Pb_0.5MnO₃ powder by rotating packed bed and its application in synthesis of diphenyl carbonate
- 化工学报 2010年第5期页码：1137-1142
- 作者机构：
  
  武汉工程大学化工与制药学院绿色化工过程省部共建教育部重点实验室，湖北省新型反应器与绿色化学工艺重点实验室
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2010-05-05，
  
  纸质出版：2010-05-05
- 稿件说明：
移动端阅览
鲁超, 金放, 袁华, 等. 超重力法制备La_0.5Pb_0.5MnO₃及其在碳酸二苯酯合成中的应用[J]. 化工学报, 2010,(5):1137-1142.

LU Chao, JIN Fang, YUAN Hua, et al. Preparation of La_0.5Pb_0.5MnO₃ powder by rotating packed bed and its application in synthesis of diphenyl carbonate[J]. CIESC Journal, 2010, (5): 1137-1142.
鲁超, 金放, 袁华, 等. 超重力法制备La_0.5Pb_0.5MnO₃及其在碳酸二苯酯合成中的应用[J]. 化工学报, 2010,(5):1137-1142. DOI：

LU Chao, JIN Fang, YUAN Hua, et al. Preparation of La_0.5Pb_0.5MnO₃ powder by rotating packed bed and its application in synthesis of diphenyl carbonate[J]. CIESC Journal, 2010, (5): 1137-1142. DOI：

摘要

采用液液相共沉淀法在旋转填充床中合成钙钛矿型复合氧化物La0.5Pb0.5MnO3的前驱体，再经高温焙烧后制备出碳酸二苯酯合成催化剂的载体材料。考察了旋转填充床转速、反应物流量和添加分散剂PEG对La0.5Pb0.5MnO3物性的影响，通过XRD、BET、SEM、粒度分析手段对载体进行表征。结果表明，旋转填充床转速为1200 r·min-1，反应物流量为80 L·h-1，加入PEG10000时可制备出纯晶相的钙钛矿载体，相应的载钯(Pd占载体质量的0.5%)催化剂在氧化羰基化合成碳酸二苯酯反应中的活性最好。当反应总压为5 MPa、CO/O2分压比为96∶6、反应时间3 h、反应温度65℃时，碳酸二苯酯收率可达13.30%。

Abstract

The precursor of perovskite-type La0.5Pb0.5MnO3 oxide was prepared by co-precipitation method in rotating packed bed (RPB).The effects of rotating speed of RPB

flow rates of reactants and the addition of PEG10000 on properties of La0.5Pb0.5MnO3 powder were investigated in combination with XRD

BET and SEM techniques.The results showed that the suitable conditions for preparation of precursor were as follows: rotating speed of 1200 r·min-1

reactants flow rate of 80 L·h-1 and PEG10000 as disperser.The corresponding La0.5Pb0.5MnO3 powder obtained by calcined was used as supports for Pd- catalytic synthesis of diphenyl carbonate（DPC） and showed good performance.The yield of DPC could achieve 13.30% when reaction temperature was 65℃

p=5 MPa

p(CO)∶p(O2)=94∶6

and reaction time 3 h.

关键词

Keywords

references

浏览量

640

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

V-Cu氧化物催化碳酸二甲酯与苯酚酯交换反应

非均相催化一步合成碳酸二苯酯ⅨCe的添加方法对Pd-Sn催化剂性能的影响

新型超细包覆型催化剂的制备及催化苯酚氧化羰基化合成碳酸二苯酯

基于递归特性和CNN的上升管内气液两相流型识别研究

稀土Y2O3基催化涂层对金属纤维表面燃烧器NO排放控制及工程验证