- 含CdS/偶氮分子的PMMA/SiO₂纳米复合二阶非线性光学材料的制备与性能
- Preparation of PMMA/SiO₂ composite material containing CdS/azo-dye molecules and its second-order nonlinear optical properties
- 化工学报 2008年第4期页码：1044-1050
- 作者机构：
  
  1. 武汉理工大学材料复合新技术国家重点实验室,湖北,武汉,430070
  2. 武汉工程大学材料科学与工程学院,湖北,武汉,430074
  3. 中国科学院合肥物质研究院等离子体物理研究所,安徽,合肥,230031
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2008-04-05，
  
  纸质出版：2008-04-05
- 稿件说明：
移动端阅览
赵立英, 刘长生, 官建国, 等. 含CdS/偶氮分子的PMMA/SiO₂纳米复合二阶非线性光学材料的制备与性能[J]. 化工学报, 2008,(4):1044-1050.

ZHAO Liying, LIU Changsheng, GUAN Jianguo, et al. Preparation of PMMA/SiO₂ composite material containing CdS/azo-dye molecules and its second-order nonlinear optical properties[J]. CIESC Journal, 2008, (4): 1044-1050.
赵立英, 刘长生, 官建国, 等. 含CdS/偶氮分子的PMMA/SiO₂纳米复合二阶非线性光学材料的制备与性能[J]. 化工学报, 2008,(4):1044-1050. DOI：

ZHAO Liying, LIU Changsheng, GUAN Jianguo, et al. Preparation of PMMA/SiO₂ composite material containing CdS/azo-dye molecules and its second-order nonlinear optical properties[J]. CIESC Journal, 2008, (4): 1044-1050. DOI：

摘要

以γ-缩水甘油醚基丙基三甲氧基硅烷(KH-560)为偶联剂，用溶胶-凝胶法合成了含4-(4′-对硝基偶氮苯)-3-氨基-苯胺(DAB)生色团的键合型有机/无机复合非线性光学材料。以掺杂的方式引入表面用AOT修饰的纳米CdS微粒。在160℃、6000 V条件下经电晕电场极化后，只含DABASD的聚合物膜极化后序参数Ф值为0.278，二阶非线性光学系数(d33)值为7.784×10-9esu，含CdS/DABASD的聚合物膜极化后序参数Ф值为0.375，d33值为7.556×10-7esu。在150℃、7000 V条件下经电晕电场极化1h后d33可达8.638×10-7esu。这种有机生色团与无机玻璃键合形成的交联网络结构中，无机玻璃的刚性三维结构能有效抑制NLO生色团的极化松弛。去极化实验结果表明，复合材料的非线性光学性能的常温稳定性好，在100℃放置400 h序参数仍保持初值的95％以上。

Abstract

A new kind of bonded organic/inorganic composite second-order nonlinear optical(NLO) material containing 4-(4′-nitrophenyl-diazenyl)phenyl-1

3-diamine azobenzene (DAB) was synthesized through the sol-gel process by using 3-glycidoxy -propyltrimethoxysilane (KH-560) as coupler agent.The CdS nanoparticles surface-capped with AOT-SO-3［(bis- 2- ethylhexyl)sulfosuccinate］ was doped into the above nanocomposites NLO material.After corona polarization at 160℃ and 6000V for 1 h

with CdS content increasing

the polarized film order parameter increased from 0.278 to 0.375 and second-order NLO coefficient increased from 7.784× 10-9esu to 7.556×10-7esu.After corona polarization of the film at 150℃ and 7000 V for 1 h

the second-order NLO coefficient could reach 8.638×10-7esu according to one dimensional rigid oriented gas model (1DROGM).The three-dimensional networks could restrict the dipole alignment relaxation of NLO chromophores.The results showed that this bonded polymer film had a high NLO capability at room temperature.The order parameter could maintain about 95% of its initial value at 100℃ for 400 h.

关键词

Keywords

references

浏览量

545

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

原子转移自由基聚合法合成PS-g-PMMA

溶胶-凝胶法制备PET/SiO2纳米复合材料及其TG、DSC分析

Pd-Pb/Al2O3催化剂上甲基丙烯醛氧化酯化合成甲基丙烯酸甲酯

甲基丙烯醛氧化酯化制备甲基丙烯酸甲酯

双官能团引发剂引发甲基丙烯酸甲酯的聚合速率

含CdS/偶氮分子的PMMA/SiO2纳米复合二阶非线性光学材料的制备与性能

Preparation of PMMA/SiO2 composite material containing CdS/azo-dye molecules and its second-order nonlinear optical properties

DOI：

摘要

Abstract

关键词

Keywords

references

含CdS/偶氮分子的PMMA/SiO₂纳米复合二阶非线性光学材料的制备与性能

Preparation of PMMA/SiO₂ composite material containing CdS/azo-dye molecules and its second-order nonlinear optical properties