- 单相金属间化合物SbSn的制备、表征及其对原油降黏
- Preparation, characterization and viscosity reduction for crude oil of single-phase SbSn intermetallic compound
- 化工学报 2007年第7期页码：1863-1867
- 作者机构：
  
  南京工业大学化学化工学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2007-07-05，
  
  纸质出版：2007-07-05
- 稿件说明：
移动端阅览
王勇, 方显力, 云志. 单相金属间化合物SbSn的制备、表征及其对原油降黏[J]. 化工学报, 2007,(7):1863-1867.

WANG Yong, FANG Xianli, YUN Zhi. Preparation, characterization and viscosity reduction for crude oil of single-phase SbSn intermetallic compound[J]. CIESC Journal, 2007, (7): 1863-1867.
王勇, 方显力, 云志. 单相金属间化合物SbSn的制备、表征及其对原油降黏[J]. 化工学报, 2007,(7):1863-1867. DOI：

WANG Yong, FANG Xianli, YUN Zhi. Preparation, characterization and viscosity reduction for crude oil of single-phase SbSn intermetallic compound[J]. CIESC Journal, 2007, (7): 1863-1867. DOI：

摘要

通过机械合金化（球磨法）制备金属间化合物SbSn，采用XRD、DSC、XPS等一系列分析手段对其相结构、熔点和表层元素的价电子态进行表征。实验在外加电场的情况下，以负载在丝网上的SbSn为吸附剂，考察静态法对原油乳状液的降粘效果。结果表明，以W（10）/O（90）为例，水浴温度恒定在20℃下，在表面活性剂用量为0.17%～0.20%，反应时间在8h后，电压规定在6.84V下，实验测定原油乳状液的粘度从8500mPa8226;s降低到3000mPa8226;s，推测可能原油乳状液中的极性物质在电流的诱导下与SbSn的表层发生化学吸附。

Abstract

A SbSn intermetallic compound was prepared via mechanical alloying（ball milling）.The bulk phase structure

melting point and valence electron state on the surface layer were detected by XRD

DSC and XPS.Using SbSn supported on wire net as adsorbent

reducing viscosity behavior for crude oil emulsion was investigated through the static method under electric field.When the temperature was maintained at 20℃

the surfactant addition was 0.17%—0.20%

reaction time was over 8 h

voltage was assigned at 6.84 V

the viscosity of emulsion with W (10)/O (90) decrease from 8500 mPa·s to 3000 mPa·s determined with rotation viscometer.It was hypothesized there was electrochemistry reaction between polar matter in emulsion and SbSn surface under electric current induction.

关键词

Keywords

references

浏览量

279

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

金属间化合物SbSn的掺Al制备及原油乳液脱硫

电场强化乙醚自然对流和池沸腾换热

电场强化乙酸乙酯自然对流和沸腾换热的实验研究

外加电场对弱导电工质管外沸腾传热强化的实验研究

余热梯级驱动热湿调控系统性能影响分析及应用