VSA-SA/PS固定载体复合膜的制备及其CO<sub>2</sub>/CH<sub>4</sub>分离性能

张颖; 王志; 伊春海; 王纪孝; 王世昌

您当前的位置：

首页 >

文章列表页 >

VSA-SA/PS固定载体复合膜的制备及其CO₂/CH₄分离性能

材料科学与工程 | 更新时间：2025-12-10

- VSA-SA/PS固定载体复合膜的制备及其CO₂/CH₄分离性能
- Preparation and performance of VSA-SA/PS fixed carrier membrane for CO₂/CH₄ separation
- 化工学报 2006年第1期页码：163-168
- 作者机构：
  
  天津大学化工学院化学工程研究所,天津,300072
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2006-01-25，
  
  纸质出版：2006-01-25
- 稿件说明：
移动端阅览
张颖, 王志, 伊春海, 等. VSA-SA/PS固定载体复合膜的制备及其CO₂/CH₄分离性能[J]. 化工学报, 2006,(1):163-168.

ZHANG Ying, WANG Zhi, YI Chunhai, et al. Preparation and performance of VSA-SA/PS fixed carrier membrane for CO₂/CH₄ separation[J]. CIESC Journal, 2006, (1): 163-168.
张颖, 王志, 伊春海, 等. VSA-SA/PS固定载体复合膜的制备及其CO₂/CH₄分离性能[J]. 化工学报, 2006,(1):163-168. DOI：

ZHANG Ying, WANG Zhi, YI Chunhai, et al. Preparation and performance of VSA-SA/PS fixed carrier membrane for CO₂/CH₄ separation[J]. CIESC Journal, 2006, (1): 163-168. DOI：

摘要

以自由基共聚合和水解的方法合成了一种新型的CO2固定载体膜材料N-乙烯基-γ-氨基丁酸钠-丙烯酸钠共聚物 (VSA-SA).以VSA-SA为表层，聚砜超滤膜为支撑体制得复合膜.研究了复合膜对CO2/CH4体系的渗透选择性，考察了金属离子交联剂和交联时间以及进料气组成对复合膜性能的影响.本文制得的复合膜运行1周仍能维持良好的分离因子和CO2渗透速率.

Abstract

A kind of new fixed carrier membrane material for CO2 separation

N-vinyl-γ-sodium aminobutyrate-sodium acrylate copolymer(VSA-SA)

was synthesized by radical copolymerization and hydrolysis. The composite membrane was developed with VSA-SA as an active layer and polysulfone (PS) ultra-filtration membrane as the support. Several kinds of metal ion cross-linkers were used to improve the performance of the composite membrane. The effects of cross-linking time on the cross-linked membrane were also studied. The membrane performance was investigated by using feed gases with different ratios of CO2 to CH4.The results showed that the composite membrane was more suitable for the separation and removal of the natural gas with high CH4 content. The prepared membrane was stable during one week testing.

关键词

Keywords

references

浏览量

406

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

硼掺杂氮基石墨烯检测变压器油中溶解气体CO和CO2的密度泛函理论研究

核壳纳米材料制备及其在CO/CO2热催化加氢中的应用

N2优先渗透ZIF-8复合膜的制备及其CO2捕集

CO2-C2H6共沸物分离的立方型状态方程选取

Li3VO4修饰富镍LiNi0.8Co0.1Mn0.1O2正极材料的电化学性能

VSA-SA/PS固定载体复合膜的制备及其CO2/CH4分离性能

Preparation and performance of VSA-SA/PS fixed carrier membrane for CO2/CH4 separation

DOI：

摘要

Abstract

关键词

Keywords

references

VSA-SA/PS固定载体复合膜的制备及其CO₂/CH₄分离性能

Preparation and performance of VSA-SA/PS fixed carrier membrane for CO₂/CH₄ separation