炭黑/P123双重模板体系原位组装梯度孔材料

崔匀; 刘洪涛; 金君素; 徐春艳; 张泽廷

您当前的位置：

首页 >

文章列表页 >

炭黑/P123双重模板体系原位组装梯度孔材料

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 炭黑/P123双重模板体系原位组装梯度孔材料
- Synthesis of hydrothermally stable composites with graded pores via insitu assembly of zeolite Y precursors by carbon black/P123 dual templates
- 化工学报 2008年第10期页码：2668-2675
- 作者机构：
  
  1. 北京化工大学理学院现代催化研究所
  2. 北京化工大学化学工程学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2008-10-05，
  
  纸质出版：2008-10-05
- 稿件说明：
移动端阅览
崔匀, 刘洪涛, 金君素, 等. 炭黑/P123双重模板体系原位组装梯度孔材料[J]. 化工学报, 2008,(10):2668-2675.

CUI Yun, LIU Hongtao, JIN Junsu, et al. Synthesis of hydrothermally stable composites with graded pores via insitu assembly of zeolite Y precursors by carbon black/P123 dual templates[J]. CIESC Journal, 2008, (10): 2668-2675.
崔匀, 刘洪涛, 金君素, 等. 炭黑/P123双重模板体系原位组装梯度孔材料[J]. 化工学报, 2008,(10):2668-2675. DOI：

CUI Yun, LIU Hongtao, JIN Junsu, et al. Synthesis of hydrothermally stable composites with graded pores via insitu assembly of zeolite Y precursors by carbon black/P123 dual templates[J]. CIESC Journal, 2008, (10): 2668-2675. DOI：

摘要

采用炭黑/P123(聚环氧乙烯醚聚环氧丙烯醚聚环氧乙烯醚三嵌段聚合物，即EO20O70EO20，平均相对分子质量5800)双重模板剂，对Y型分子筛前驱体进行组装合成了具有原位梯度孔及高水热稳定性的材料。FT-IR结果表明，组装过程将Y型分子筛的初级和次级结构单元引入分子筛的孔壁之中。BET和TEM结果表明，材料具有相互贯通的梯度孔道(0.39 nm-3.8 nm-6.5 nm-19.9 nm)，比表面积693 m2·g-1，孔容1.89ml·g-1。在800℃、100％水蒸气处理2 h和4 h后，比表面积保留率分别为80.1%和35.1%，孔容保留率分别为45.0%和25.4%。为重油大分子的催化裂化提供了一种具有潜在应用价值的材料。

Abstract

A series of hydrothermally stable composites with graded pores were synthesized via insitu assembly of zeolite Y precursors by carbon black/P123 templatesThe graded composites were characterized by means of XRD

FT-IR

TEM

BET and NH3-TPDThe results of FT-IR showed that the primary and secondary structural building units of zeolite Y were introduced into the wall of zeolitesThe results of BET and TEM suggested that the composites had interconnected hierarchical pore structure (0.39 nm-3.8 nm-6.5 nm-19.9 nm).The surface area and pore volume were 693 m2·g-1 and 1.89 ml·g-1 respectivelyAfter hydrothermal treatment at 100% steam

800℃ for 2 h and 4 h

the remaining fractions of surface area were 80.1% and 35.1% respectively

while the remaining fractions of pore volume were 45.0% and 25.4% respectivelyThe present paper provides a novel route for fabricating materials with graded pores and high hydrothermal stability which are candidates for heavy oil cracking catalysts.

关键词

Keywords

references

浏览量

967

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

机器学习在结晶过程建模与控制中的研究进展

基于GLAE-MLP的炼化装置管道腐蚀健康状态评估方法

部分预混旋流燃烧入口激励下的熵波产生及耗散机制研究

旋流式冷却造粒塔的优势与风险分析

基于富氮席夫碱网络聚合物的混合基质膜及其CO2分离性能