溶胶-凝胶法制备PET/SiO₂纳米复合材料及其TG、DSC分析

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 溶胶-凝胶法制备PET/SiO₂纳米复合材料及其TG、DSC分析
- Poly(ethylene terephthalate)/SiO₂ nanocomposites prepared by sol-gel method and their TG & DSC analysis
- 化工学报 2007年第11期页码：2926-2931
- 作者机构：
  
  青岛大学纤维新材料与现代纺织国家重点实验室培育基地
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2007-11-05，
  
  纸质出版：2007-11-05
- 稿件说明：
移动端阅览
王孝龙, 纪全, 孔庆山, 等. 溶胶-凝胶法制备PET/SiO₂纳米复合材料及其TG、DSC分析[J]. 化工学报, 2007,(11):2926-2931.

WANG Xiaolong, JI Quan, KONG Qingshan, et al. Poly(ethylene terephthalate)/SiO₂ nanocomposites prepared by sol-gel method and their TG & DSC analysis[J]. CIESC Journal, 2007, (11): 2926-2931.
王孝龙, 纪全, 孔庆山, 等. 溶胶-凝胶法制备PET/SiO₂纳米复合材料及其TG、DSC分析[J]. 化工学报, 2007,(11):2926-2931. DOI：

WANG Xiaolong, JI Quan, KONG Qingshan, et al. Poly(ethylene terephthalate)/SiO₂ nanocomposites prepared by sol-gel method and their TG & DSC analysis[J]. CIESC Journal, 2007, (11): 2926-2931. DOI：

摘要

采用溶胶-凝胶（sol-gel）法，将正硅酸乙酯和水加入到制备聚对苯二甲酸乙二酯（PET）的中间产物对苯二甲酸双羟乙酯(BHET)中

在液态下均匀混合，高温下快速发生溶胶-凝胶反应，再按PET缩聚反应制得PET/SiO2纳米复合材料。通过TEM、TG、DSC对材料进行了表征和研究。结果表明，SiO2在PET中均匀分散，其尺寸在10～100 nm之间，PET/SiO2纳米复合材料的热降解活化能较普通PET有明显提高，但初始降解温度和结晶性能均有所降低。

Abstract

Poly(ethylene terephthalate)(PET)/SiO2 nanocomposites were synthesized via the sol-gel method that involved two steps: terephthalic acid first reacted with excess ethylene glycol to form bis(hydroxyethyl) terephthalate (BHET); tetraethoxysilane (TEOS) was added into the BHET

and the sol-gel reactions proceeded at a high temperature to form the silica nanonetwork concurrent with polycondensation of BHET to produce the PET matrix.Transmission electron microscopy (TEM) showed that the sizes of silica particles were at nanoscale

and the nanoparticles were uniformly dispersed in the polymer matrix.Thermogravimetric analysis (TGA) results indicated that the activation energy of thermal degradation of the composites was largely increased.The nonisothermal crystallization ability of the composites was found to decrease according to differential scanning calorimetry (DSC).

关键词

Keywords

references

浏览量

263

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

芳纶浆粕增强丁腈橡胶复合材料的摩擦磨损性能

废纸基电路板非金属材料性质及其复合材料性能

纳米活性炭/锌锰复合电极材料的制备及性能

硫酸盐晶须改性ABS复合材料的性能与微观结构

γ-Al2O3中孔陶瓷膜的制备及表征

溶胶-凝胶法制备PET/SiO2纳米复合材料及其TG、DSC分析

Poly(ethylene terephthalate)/SiO2 nanocomposites prepared by sol-gel method and their TG & DSC analysis

DOI：

摘要

Abstract

关键词

Keywords

references

溶胶-凝胶法制备PET/SiO₂纳米复合材料及其TG、DSC分析

Poly(ethylene terephthalate)/SiO₂ nanocomposites prepared by sol-gel method and their TG & DSC analysis