- Properties of D-tryptophane molecular imprinting composite membranes and its preparation
- 化工学报 2007年第1期
- 作者机构：
  
  1. 华东理工大学化学工程研究所
  2. 上海应用技术学院化学工程系
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2007-01-05，
  
  纸质出版：2007-01-05
- 稿件说明：
移动端阅览
杨座国, 许振良, 陈桂娥, 等. D-色氨酸印迹中空纤维复合膜制备及其性能[J]. 化工学报, 2007,(1).

YANG Zuoguo, XU Zhenliang, Chen Gui’e, et al. Properties of D-tryptophane molecular imprinting composite membranes and its preparation[J]. CIESC Journal, 2007, (1).
杨座国, 许振良, 陈桂娥, 等. D-色氨酸印迹中空纤维复合膜制备及其性能[J]. 化工学报, 2007,(1). DOI：

YANG Zuoguo, XU Zhenliang, Chen Gui’e, et al. Properties of D-tryptophane molecular imprinting composite membranes and its preparation[J]. CIESC Journal, 2007, (1). DOI：

摘要

以聚砜（PSF）中空纤维超滤膜为基膜，采用表面紫外光聚合方法制备了D-色氨酸印迹中空纤维复合膜(CMIHFCM)。由SEM分析表明经过表面聚合后的D-色氨酸印迹中空纤维复合膜表面具有层叠交联状复合层，其厚度约3 μm。实验结果表明D-色氨酸印迹中空纤维复合膜对模板分子D-色氨酸具有很好的识别作用，D

L-色氨酸的分离因子（α）最高可以达到5.0，大于非分子印迹复合膜的识别选择性。此外，引发剂的用量对D-色氨酸印迹中空纤维复合膜的识别性能有较大影响；当引发剂的浓度为1.0％，制得的D-色氨酸印迹中空纤维复合膜对D-色氨酸具有较好的识别性能，具有良好的应用前景。

Abstract

Using polysulfone (PSF) hollow fiber membrane as the supporting membrane

chiral (D-tryptophane) molecular imprinted hollow fiber composite membrane (CMIHFCM) was fabricated by the surface photo-polymerization method and the recognition ability of CMIHFCM for D

L-tryptophane was studied.After surface polymerization

the external surface of CMIHFCM had a complex network layer with a thickness of 3 μm on the supporting membrane.The experimental results showed that CMIHFCM had the recognition ability for the template D-tryptophane.The D- tryptophane solution could be condensed more significantly by the molecular imprinted membrane than L-tryptophane

and the separation factor (α) of D- tryptophane (D-Trp) and L-tryptophane (L-Trp) could be 5.0.However

the recognition for D-tryptophane by the non-molecular imprinted membrane was weaker.When the concentration of initiator was 1.0%

CMIHFCM with good recognition ability for D-Trp was obtained.

关键词

Keywords

references

浏览量

270

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基于机器学习算法的生物质热解产物产率预测研究

相变悬浮液射流冲击变形状多孔层覆盖壁面的热分析

一种顺序式模拟移动床混合建模与优化策略

磷酸钒锂正极材料的氮掺杂碳包覆与Ti4+共掺杂协同改性研究

过渡金属基氮掺杂炭的构筑及其脱硫性能研究