聚3，4-乙烯二氧噻吩聚苯乙烯磺酸复合LB膜对有机电致发光器件性能的优化

郑华靖; 蒋亚东; 徐建华; 杨亚杰

您当前的位置：

首页 >

文章列表页 >

聚3，4-乙烯二氧噻吩聚苯乙烯磺酸复合LB膜对有机电致发光器件性能的优化

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 聚3，4-乙烯二氧噻吩聚苯乙烯磺酸复合LB膜对有机电致发光器件性能的优化
- Performance optimization of OLED device with LB film of PEDOT-PSS
- 化工学报 2010年第6期页码：1582-1586
- 作者机构：
  
  1. 电子科技大学光电信息学院
  2. 电子薄膜与集成器件国家重点实验室
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2010-06-05，
  
  纸质出版：2010-06-05
- 稿件说明：
移动端阅览
郑华靖, 蒋亚东, 徐建华, 等. 聚3，4-乙烯二氧噻吩聚苯乙烯磺酸复合LB膜对有机电致发光器件性能的优化[J]. 化工学报, 2010,(6):1582-1586.

ZHENG Huajing, JIANG Yadong, XU Jianhua, et al. Performance optimization of OLED device with LB film of PEDOT-PSS[J]. CIESC Journal, 2010, (6): 1582-1586.
郑华靖, 蒋亚东, 徐建华, 等. 聚3，4-乙烯二氧噻吩聚苯乙烯磺酸复合LB膜对有机电致发光器件性能的优化[J]. 化工学报, 2010,(6):1582-1586. DOI：

ZHENG Huajing, JIANG Yadong, XU Jianhua, et al. Performance optimization of OLED device with LB film of PEDOT-PSS[J]. CIESC Journal, 2010, (6): 1582-1586. DOI：

摘要

采用Langmuir-Blodgett（LB）膜诱导沉积法制备聚3，4-乙烯二氧噻吩高度有序导电聚合物复合薄膜，研究了薄膜的导电性能并进一步研究薄膜在改善器件性能方面的作用。将其应用于有机电致发光二极的空穴缓冲层，将聚3，4-乙烯二氧噻吩聚苯乙烯磺酸复合LB膜沉积于铟锡氧化物（ITO）电极上，制备了以复合LB膜为空穴缓冲层的有机电致发光二极。发现复合LB膜改善了器件性能（启动电压降低、最大亮度增加），但进一步的研究表明，LB膜器件在一定时间后出现性能劣化，X射线反射率（XRR）分析表明薄膜的结构发生一定程度的改变，是导致器件性能变差的可能原因。

Abstract

Due to its high conductivity and stability，good optical transparency characteristics and easy synthesis，poly（3，4-ethylenedioxythiophene）（PEDOT）has wide application prospects in the antistatic coating，organic，display device，energy storage transformation，sensor，etc.in recent years.A Langmuir-Blodgett（LB）inducing method was firstly used to prepare single layer and multilayer conducting composite poly（3，4-ethylenedioxythiophene）-poly（styrenesulfonate）（PEDOT-PSS）film. The application of PEDOT nanostructure to improving organic electric device performance of organic light-emitting diode（OLED）was studied.Furthermore，this conducting polymeric LB film was utilized as the hole transfer layer in the OLED device，and efficiency enhancement by carrier injection was observed，which was ascribed to the ordered structure of this film.However，further investigation showed that this PEDOT-PSS film had inferior structure ability.

关键词

Keywords

references

浏览量

229

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

含湿率对多孔介质热导率测量准确性的影响

基于热质传递解耦特性的溶液除湿过程传热传质系数(Ⅱ)实验与Le-hD分离测量法应用

不同SK型静态混合器的流场特性及其混合效果分析

Ca（OH）2/CaO间接反应器储释热循环性能优化

TPMS-Diamond静态混合器停留时间分布特性研究