- 环氧/聚氨酯涂层在4种环境中失效行为的EIS
- Failure behaviors of epoxy/acrylic polyurethane organic coatings in corrosive media by EIS
- 化工学报 2010年第10期页码：2656-2661
- 作者机构：
  
  1. 北京化工大学理学院
  2. 北京化工大学材料学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2010-10-05，
  
  纸质出版：2010-10-05
- 稿件说明：
移动端阅览
庞然, 左禹, 唐聿明, 等. 环氧/聚氨酯涂层在4种环境中失效行为的EIS[J]. 化工学报, 2010,(10):2656-2661.

PANG Ran, ZUO Yu, TANG Yuming, et al. Failure behaviors of epoxy/acrylic polyurethane organic coatings in corrosive media by EIS[J]. CIESC Journal, 2010, (10): 2656-2661.
庞然, 左禹, 唐聿明, 等. 环氧/聚氨酯涂层在4种环境中失效行为的EIS[J]. 化工学报, 2010,(10):2656-2661. DOI：

PANG Ran, ZUO Yu, TANG Yuming, et al. Failure behaviors of epoxy/acrylic polyurethane organic coatings in corrosive media by EIS[J]. CIESC Journal, 2010, (10): 2656-2661. DOI：

摘要

用电化学交流阻抗法（EIS）研究了环氧富锌底漆/环氧云铁中间漆/丙烯酸聚氨酯面漆这一涂层体系在3.5%NaCl溶液、3.5%NaCl溶液+紫外辐射、湿热和盐雾这4种环境中的失效行为，探讨了特征频率下的相位角和涂层电阻值之间对应的关系。结果表明：中频区10 Hz处涂层相位角随时间的变化曲线和涂层电阻值随时间的变化曲线有良好的相似性，据此可以对所研究的涂层体系失效程度进行快速评价;所试验的4种腐蚀环境对所研究的涂层体系的破坏作用由小到大依次为：3.5% NaCl溶液

Abstract

Failure behaviors of the organic coating system

zinc-rich epoxy primer/epoxy coating with mica iron/acrylic polyurethane topcoat

in corrosive media

including 3.5% NaCl solution

3.5% NaCl solution + UV radiation

moist heat and salt spray

were studied with electrochemistry impedance spectra (EIS）.The relationships between coating resistance and phase angle were analyzed.The results indicated that phase angle at middle frequency of 10 Hz and coating resistance showed similar decreasing tendencies

hence these phase angle parameters may be used as quick measurements to evaluate coating performance.The order of the damaging effect of the four corrosive environments on carbon steel was 3.5% NaCl solution < salt spray < moist heat < 3.5% NaCl solution + UV radiation.

关键词

Keywords

references

浏览量

208

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

液氢贮箱在轨排气的闪蒸特性与热力态调节规律研究

富氧空位锌掺杂PdO/ZrO2催化CO2和苯酚合成碳酸二苯酯

变工况下换热网络中的热量传递规律及瓶颈识别与优化

基于机器学习算法的生物质热解产物产率预测研究

全氟聚醚分子量及其分布表征研究