超稳Y沸石封装磷钨酸的制备、表征及其催化性能

曾湘; 袁霞; 吴剑; 罗和安

您当前的位置：

首页 >

文章列表页 >

超稳Y沸石封装磷钨酸的制备、表征及其催化性能

催化、动力学与反应器 | 更新时间：2025-12-10

- 超稳Y沸石封装磷钨酸的制备、表征及其催化性能
- Preparation, characterization and catalytic behavior of phosphotungstic acid encapsulated in Y zeolite
- 化工学报 2010年第6期页码：1463-1468
- 作者机构：
  
  湘潭大学化工学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2010-06-05，
  
  纸质出版：2010-06-05
- 稿件说明：
移动端阅览
曾湘, 袁霞, 吴剑, 等. 超稳Y沸石封装磷钨酸的制备、表征及其催化性能[J]. 化工学报, 2010,(6):1463-1468.

ZENG Xiang, YUAN Xia, WU Jian, et al. Preparation, characterization and catalytic behavior of phosphotungstic acid encapsulated in Y zeolite[J]. CIESC Journal, 2010, (6): 1463-1468.
曾湘, 袁霞, 吴剑, 等. 超稳Y沸石封装磷钨酸的制备、表征及其催化性能[J]. 化工学报, 2010,(6):1463-1468. DOI：

ZENG Xiang, YUAN Xia, WU Jian, et al. Preparation, characterization and catalytic behavior of phosphotungstic acid encapsulated in Y zeolite[J]. CIESC Journal, 2010, (6): 1463-1468. DOI：

摘要

采用“瓶中造船”方法制备了超稳Y沸石封装的磷钨酸催化剂PW-USY，并用FT-IR、UV-vis，N2吸附，NH3-TPD等手段对其进行了表征，并与浸渍法制备的负载催化剂PW/USY进行了比较，结果表明在超稳Y沸石超笼中成功合成了具有Keggin结构的12-磷钨酸。在以H2O2为氧源的环己酮氨肟化反应中，封装型磷钨酸催化剂表现出较好的催化活性，选择性较纯磷钨酸有所降低。封装型磷钨酸催化剂重复使用5次后，催化性能没有明显的下降，较负载型磷钨酸而言能较好地解决活性组分流失的问题，显示出潜在的应用前景。

Abstract

Phosphotungstic acid encapsulated in ultra stable Y zeolite (PW-USY) was prepared by the “ship in the bottle” synthesis.The obtained catalysts were characterized with FT-IR

ICP

UV-vis

N2-adsorption

XRD and SEM techniques.Compared with immobilized catalysts (PW/USY)

it was demonstrated that encapsulation of Keggin-type 12-phosphotungstic acid in the supercage of USY zeolite was realized.In the ammoximation of cyclohexanone system with H2O2 as oxygen source

PW-USY showed better catalytic activity than PW/USY.Moreover

the catalytic performance of PW-USY did not drop apparently after using five times

and could solve the leakage problem of active component in polar reaction media better than immobilized catalysts (PW/USY).

关键词

Keywords

references

浏览量

497

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

固体蓄冷填充床性能提升及保冷特性研究

原位水热法可控合成Bi2MoO6/MoO3复合纤维及其高效光催化产氢性能

塔式太阳能辅助超临界压缩CO2储能系统热力学性能

碱金属改性对SrMnO3催化乙苯化学链氧化脱氢性能的影响规律研究

电子效应精准调控的纳米金催化剂在低碳多元醇选择性氧化研究进展