- 甲基三甲氧基硅烷改性硅溶胶憎水膜的制备
- Preparation of hydrophobic coatings with methyltrimethoxysilane modified Si-sol
- 化工学报 2009年第9期页码：2398-2403
- 作者机构：
  
  1. 先进土木材料教育部重点实验室（同济大学）
  2. 同济大学材料科学与工程学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2009-09-05，
  
  纸质出版：2009-09-05
- 稿件说明：
移动端阅览
王国建, 石全, 沙海祥, 等. 甲基三甲氧基硅烷改性硅溶胶憎水膜的制备[J]. 化工学报, 2009,(9):2398-2403.

WANG Guojian, SHI Quan, SHA Haixiang, et al. Preparation of hydrophobic coatings with methyltrimethoxysilane modified Si-sol[J]. CIESC Journal, 2009, (9): 2398-2403.
王国建, 石全, 沙海祥, 等. 甲基三甲氧基硅烷改性硅溶胶憎水膜的制备[J]. 化工学报, 2009,(9):2398-2403. DOI：

WANG Guojian, SHI Quan, SHA Haixiang, et al. Preparation of hydrophobic coatings with methyltrimethoxysilane modified Si-sol[J]. CIESC Journal, 2009, (9): 2398-2403. DOI：

摘要

制备了用于增强玻璃表面憎水性的甲基三甲氧基硅烷（MTMS）/硅溶胶/丙烯酸羟丙酯透明薄膜。讨论了MTMS的水解温度、pH值、MTMS与硅溶胶的反应时间、MTMS用量与薄膜憎水性的关系。采用红外光谱和原子力显微镜表征了涂膜表面的官能团种类、数量和微观结构。研究表明，将MTMS在40℃、pH=3的条件下水解，再与酸性硅溶胶的体积比（r）为0.1，在60℃下反应2 h，所得的产物制备的涂膜的憎水性最好，水接触角可达127°。

Abstract

Transparent hydrophobic methyltrimethoxysilane(MTMS)/Si-sol/hydroxypropyl acrylate coatings was prepared in order to improve the hydrophobicity of glass surface.Effects of the hydrolysis temperature of MTMS

the pH value of hydrolization solution

the reaction time of MTMS with Si-sol

and the MTMS content on the hydrophobicity of the coatings were discussed respectively.The type and amount of functional groups on the coating’s surface as well as the microstructure were characterized by Fourier transform infrared spectroscopy(FTIR)and atomic force microscope.The coatings with the best hydrophobicity was found when prepared with the following conditions: the MTMS was hydrolyzed in 40℃

pH=3

and the volume ratio of the hydrolyzed MTMS and Si-sol was 0.1

the reaction time was 2 h and the reaction temperature was 60℃.

关键词

Keywords

references

浏览量

829

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

改性硅溶胶憎水薄膜的制备

稀土Y2O3基催化涂层对金属纤维表面燃烧器NO排放控制及工程验证

Ca（OH）2/CaO间接反应器储释热循环性能优化

机器学习在结晶过程建模与控制中的研究进展

基于富氮席夫碱网络聚合物的混合基质膜及其CO2分离性能