- 核壳结构半导体纳米晶体CdS/ZnS的制备及其光学性质
- Synthesis of CdS/ZnS core-shell quantum dots in reverse micelle system and its optical property research
- 化工学报 2009年第2期页码：519-523
- 作者机构：
  
  南京航空航天大学材料科学与技术学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2009-02-05，
  
  纸质出版：2009-02-05
- 稿件说明：
移动端阅览
李江苏, 常树全, 康斌, 等. 核壳结构半导体纳米晶体CdS/ZnS的制备及其光学性质[J]. 化工学报, 2009,(2):519-523.

LI Jiangsu, CHANG Shuquan, KANG Bin, et al. Synthesis of CdS/ZnS core-shell quantum dots in reverse micelle system and its optical property research[J]. CIESC Journal, 2009, (2): 519-523.
李江苏, 常树全, 康斌, 等. 核壳结构半导体纳米晶体CdS/ZnS的制备及其光学性质[J]. 化工学报, 2009,(2):519-523. DOI：

LI Jiangsu, CHANG Shuquan, KANG Bin, et al. Synthesis of CdS/ZnS core-shell quantum dots in reverse micelle system and its optical property research[J]. CIESC Journal, 2009, (2): 519-523. DOI：

摘要

通过反胶束法成功制备了CdS及CdS/ZnS核壳结构量子点，采用紫外-可见吸收光谱(UV-Vis)、透射电子显微镜(TEM)、能量色散型X射线能谱(EDX)以及荧光光谱(PL)等对其结构和性能进行了研究。与CdS量子点相比，CdS/ZnS量子点的粒径明显变大，本文估算了粒子的粒径，TEM图像很好的印证了估算的结果；结合EDX的测试结果可以推断CdS/ZnS量子点的结构是ZnS包裹在CdS表面的核壳结构；CdS/ZnS量子点的荧光强度与CdS量子点相比有了明显的提高，原因主要是壳层的ZnS消除了CdS量子点表面上存在的无辐射复合中心。

Abstract

CdS and CdS/ZnS quantum dots were synthesized by the microemulsion method in sulfosuccinic acid bis(2-ethylhexyl)ester sodium salt(AOT) surfactant reverse micelles containing water.The products were characterized by UV-Vis spectrometer

transmission electronmicroscopy (TEM)

energy dispersive X-ray spectroscope (EDX)and photoluminescence(PL) spectroscope.The diameter of CdS/ZnS nanoparticle was obvious larger than that of CdS nanoparticle.The diameter of the nanoparticle was estimated

which was confirmed by the images of TEM.The existence of core-shell structure was established by the result of energy dispersive X-ray analysis. PL studies of the samples showed that the luminescence from CdS was enhanced by the ZnS shell.A possible reason was that the ZnS shell reduced the number of defects on the surface of CdS quantum dots

which were assumed to act as centers for radiation-free recombination.

关键词

Keywords

references

0

浏览量

198

下载量

0

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

相关文章

混合溶剂中十八胺含量对CdSe量子点发光性能的影响

钙循环热化学储能载能体放热特性研究

高速高温箔片端面密封热气弹耦合性能分析

压力波强化横掠管束传热实验研究

煤化工废盐中杂质对NaCl和Na2SO4溶剂化影响研究

相关作者

嵇天浩

梁辉

孙家跃

孙宝国

祝钧

葛广路

相关机构

北京工商大学化学与环境工程学院

国家纳米科学中心

⁰