- Synthesis and characterization of monovinyl-functionalized silsesquioxane cage
- 化工学报 2009年第7期页码：1831-1836
- 作者机构：
  
  特种功能高分子材料及相关技术教育部重点实验室（华东理工大学）
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2009-07-05，
  
  纸质出版：2009-07-05
- 稿件说明：
移动端阅览
刘勇, 周燕, 黄福伟, 等. 笼型单乙烯基倍半硅氧烷的合成及表征[J]. 化工学报, 2009,(7):1831-1836.

LIU Yong, ZHOU Yan, HUANG Fuwei, et al. Synthesis and characterization of monovinyl-functionalized silsesquioxane cage[J]. CIESC Journal, 2009, (7): 1831-1836.
刘勇, 周燕, 黄福伟, 等. 笼型单乙烯基倍半硅氧烷的合成及表征[J]. 化工学报, 2009,(7):1831-1836. DOI：

LIU Yong, ZHOU Yan, HUANG Fuwei, et al. Synthesis and characterization of monovinyl-functionalized silsesquioxane cage[J]. CIESC Journal, 2009, (7): 1831-1836. DOI：

摘要

用环戊基三氯硅烷合成不完全缩合三羟基硅氧烷［(C5H9)7Si7O9(OH)3］，再以乙烯基三氯硅烷和不完全缩合三羟基硅氧烷为原料，以四氢呋喃和三乙胺为混合溶剂，通过“顶角-戴帽”反应合成了笼型单乙烯基倍半硅氧烷，即1

13-七环戊基-15-乙烯基笼型倍半硅氧烷(VinylPOSS)。利用FTIR、1H NMR、29Si NMR、13C NMR、元素分析、WAXD和TGA表征了VinylPOSS的结构及热稳定性。研究结果表明VinylPOSS的产率随着反应时间的增加而提高，当反应时间为10 h时，产率高达90%；其在弱极性溶剂中具有较好的溶解性，5%失重温度为283℃，800℃残留率为56%，具有较高的热稳定性。研究了VinylPOSS和高含氢硅油(HHSF)的反应性，结果表明VinylPOSS能与含氢硅油发生α、β加成反应

且以β加成为主。

Abstract

Monovinyl-functionalized silsesquioxane cage

13-heptacyclopentyl-15-vinyl silsesquioxane(VinylPOSS)

was prepared via the corner capping reaction of incompletely condensed silsesquioxanes

(C5H9)7Si7O9(OH)3

with vinyltrichlorosilane.VinylPOSS was characterized by FTIR

1H NMR

29Si NMR

13C NMR

elemental analysis

WAXD and TGA.The yield of VinylPOSS increased with reaction time

when vinyltrichlorosilane reacted with (C5H9)7Si7O9(OH)3 for 10 h

the yield was 90%.VinylPOSS has good solubility in weak polar solvent

and it shows good thermal stability

its temperature with 5% decomposition is 283℃ and the temperature with 56% residue is 800℃.The reactivity of VinylPOSS with high hydrogen-containing silicone fluid (HHSF) was investigated.It can be reacted with HHSF by Michael additions at both α- and β- positions

and the reaction is mainly β-addition.

关键词

Keywords

references

浏览量

208

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

酯基锡（丁酯）的合成及其对PVC的加工稳定性

二甲醚氧化反应及其添加剂效应

相变悬浮液射流冲击变形状多孔层覆盖壁面的热分析

复合金属CuCr2O4表面CNCl水解反应机理

磷酸钒锂正极材料的氮掺杂碳包覆与Ti4+共掺杂协同改性研究