聚(丙烯酸-丙烯酰胺)/水滑石纳米复合高吸水性树脂的制备及表征

张亚涛; 张林; 陈欢林

您当前的位置：

首页 >

文章列表页 >

聚(丙烯酸-丙烯酰胺)/水滑石纳米复合高吸水性树脂的制备及表征

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 聚(丙烯酸-丙烯酰胺)/水滑石纳米复合高吸水性树脂的制备及表征
- Preparation and characterization of poly(acrylic acid-co-acrylamide)/hydrotalcite nanocomposite superabsorbent
- 化工学报 2008年第6期页码：1565-1570
- 作者机构：
  
  浙江大学化学工程与生物工程学系
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2008-06-05，
  
  纸质出版：2008-06-05
- 稿件说明：
移动端阅览
张亚涛, 张林, 陈欢林. 聚(丙烯酸-丙烯酰胺)/水滑石纳米复合高吸水性树脂的制备及表征[J]. 化工学报, 2008,(6):1565-1570.

ZHANG Yatao, ZHANG Lin, CHEN Huanlin. Preparation and characterization of poly(acrylic acid-co-acrylamide)/hydrotalcite nanocomposite superabsorbent[J]. CIESC Journal, 2008, (6): 1565-1570.
张亚涛, 张林, 陈欢林. 聚(丙烯酸-丙烯酰胺)/水滑石纳米复合高吸水性树脂的制备及表征[J]. 化工学报, 2008,(6):1565-1570. DOI：

ZHANG Yatao, ZHANG Lin, CHEN Huanlin. Preparation and characterization of poly(acrylic acid-co-acrylamide)/hydrotalcite nanocomposite superabsorbent[J]. CIESC Journal, 2008, (6): 1565-1570. DOI：

摘要

首先用尿素法合成了水滑石(HT)，然后用甲基丙烯磺酸钠(SMAS)对水滑石进行插层，得到了插层的水滑石(SMAS-HT)，最后通过反相悬浮聚合制备了一种新型的聚(丙烯酸-丙烯酰胺)/水滑石纳米复合高吸水性树脂，其中N

N′-亚甲基双丙烯酰胺(NMBA)为交联剂，过硫酸钾(KPS)为引发剂。通过傅里叶变换红外光谱(FTIR)、X-射线衍射(XRD)及扫描电镜(SEM)等手段表征其结构和形貌。考察了SMAS-HT的含量对其吸水(盐)性能的影响。结果表明，插入SMAS的水滑石片层在聚合后发生了剥离，添加少量的SMAS-HT可以明显提高树脂的吸水(盐)性能，当SMAS-HT含量为3.0%（质量）时，树脂的吸(盐)水性能达到最大。

Abstract

The hydrotalcite (HT) synthesized with urea method was used to prepare intercalated HT (SMAS-HT) by using methyl allyl sulfonate (SMAS) as an intercalation agent.A novel poly (acrylic acid-co-acrylamide)/HT nanocomposite superabsorbent was prepared by inverse polymerization

using N

N′-methylenebisacrylamide (NMBA) as a crosslinking agent and potassium persulfate (KPS) as an initiator.The structure and morphology were characterized by FTIR

XRD and SEM.The influences of the amount of SMAS-HT on the water (salt) absorbency were studied.The results showed that the intercalation was successful and SMAS-HT was completely exfoliated after polymerization.Adding a small amount of SMAS-HT could effectively improve the water (salt) absorbency of nanocomposite superabsorbents.The nanocomposite superabsorbents had their highest water (salt) absorbency when the content of SMAS-HT was 3.0%(mass).

关键词

Keywords

references

浏览量

413

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

铜铁尾矿制酸烧渣制备纳米Fe/SiO2核壳复合粒子的微波吸收性能

碳化钨/碳纳米管纳米复合材料的制备及其对硝基苯的电催化活性

PP/黏土纳米复合材料的结构与性能

魔芋粉-丙烯酸-丙烯酰胺接枝共聚合成高吸水树脂

腐殖酸-聚丙烯酸表面交联吸水性树脂的合成与性能