有机膨润土的制备与表征及吸附港口含油废水性能

陈捷; 冯威; 刘延; 王丽; 田斌

您当前的位置：

首页 >

文章列表页 >

有机膨润土的制备与表征及吸附港口含油废水性能

能源和环境工程 | 更新时间：2025-12-10

- 有机膨润土的制备与表征及吸附港口含油废水性能
- Preparation and characteristics of organmontmorillonite and adsorption of oily wastewater from port
- 化工学报 2008年第1期页码：228-231
- 作者机构：
  
  大连海事大学环境科学与工程学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2008-01-05，
  
  纸质出版：2008-01-05
- 稿件说明：
移动端阅览
陈捷, 冯威, 刘延, 等. 有机膨润土的制备与表征及吸附港口含油废水性能[J]. 化工学报, 2008,(1):228-231.

CHEN Jie, FENG Wei, LIU Yan, et al. Preparation and characteristics of organmontmorillonite and adsorption of oily wastewater from port[J]. CIESC Journal, 2008, (1): 228-231.
陈捷, 冯威, 刘延, 等. 有机膨润土的制备与表征及吸附港口含油废水性能[J]. 化工学报, 2008,(1):228-231. DOI：

CHEN Jie, FENG Wei, LIU Yan, et al. Preparation and characteristics of organmontmorillonite and adsorption of oily wastewater from port[J]. CIESC Journal, 2008, (1): 228-231. DOI：

摘要

利用十八烷基三甲基溴化铵改性钠基膨润土（Na-MMT）制备了有机膨润土（O-MMT）。利用傅里叶红外光谱仪、X射线衍射仪、透射电镜和吸附仪表征了其形貌和结构特征。结果表明有机离子通过离子交换作用进入钠基膨润土层间，d001晶面间距由1.26 nm增加到3.80 nm。利用其作为吸附剂，研究其处理港口含油废水的性能。与Na-MMT对比，O-MMT对油和COD的去除率分别是Na-MMT的2.5倍和5倍。通过研究搅拌时间、吸附剂的用量和循环使用次数对吸附性能的影响，表明室温下，投加2 % 吸附剂，搅拌30 min是处理含油港口废水的最佳条件，该吸附剂可循环使用3次。

Abstract

Organmontmorillonite (O-MMT) was modified by surfactant-octadecyltrimethylammonium bromide with Na-montmorollonite (Na-MMT).The characteristics and structure of the sorbent were investigated by Fourier transform infrared ray spectroscopy (FT-IR)

X-ray diffraction (XRD)

transmission electron microscope (TEM) and BET analysis.The results indicated that organic cations were exchanged into Na-MMTs stacks and the basal spacing (d001) increased from 1.26 nm to 3.80 nm.Then O-MMT was used as sorbent to treat oily wastewater from port.Comparing to Na-MMT

the COD (chemical oxygen demand) and oil removal increased by 5.0 times and 2.5 times

respectively .The effects of agitation time

the amount of O-MMT and recycle times of O-MMT were investigated and the optimum experiment condition at room temperature was established: adding 2.0 % O-MMT and agitating 30 min.The duty-cycle operation of O-MMT was three times.

关键词

Keywords

references

浏览量

152

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Fe-Zn基废脱硫剂制备铁碳材料及其对废水微电解性能

多因素对反硝化除磷过程中COD、N和P的去除分析

不同来源家庭户用沼气池沼液成分分析及风险评价

多乙烯多胺胺化大孔GMA-DVB树脂的合成及其对金属离子的吸附

基于电化学技术检测微生物吸附