- MMA/BA共聚物改性的水性聚氨酯的合成与表征
- Synthesis of aqueous polyurethane modified by methyl  methacrylate and butyl acrylate copolymer
- 化工学报 2007年第7期页码：1851-1856
- 作者机构：
  
  华南理工大学化工与能源学院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2007-07-05，
  
  纸质出版：2007-07-05
- 稿件说明：
移动端阅览
胡国文, 黄洪, 傅和青, 等. MMA/BA共聚物改性的水性聚氨酯的合成与表征[J]. 化工学报, 2007,(7):1851-1856.

HU Guowen, HUANG Hong, FU Heqing, et al. Synthesis of aqueous polyurethane modified by methyl  methacrylate and butyl acrylate copolymer[J]. CIESC Journal, 2007, (7): 1851-1856.
胡国文, 黄洪, 傅和青, 等. MMA/BA共聚物改性的水性聚氨酯的合成与表征[J]. 化工学报, 2007,(7):1851-1856. DOI：

HU Guowen, HUANG Hong, FU Heqing, et al. Synthesis of aqueous polyurethane modified by methyl  methacrylate and butyl acrylate copolymer[J]. CIESC Journal, 2007, (7): 1851-1856. DOI：

摘要

以1

4-丁二醇 (BDO)、二羟甲基丙酸 (DMPA) 和己二酸二酰肼 (ADH) 为扩链剂，以甲基丙烯酸甲酯 (MMA) 和丙烯酸丁酯 (BA) 改性聚氨酯 (PU)，得聚氨酯-丙烯酸酯复合乳液 (PUA).研究了BA和二丙酮丙烯酰胺 (DAAM) 对乳液及膜性能和粘接性能的影响，并用傅立叶红外光谱 (FTIR)仪对PUA复合乳液进行了结构表征.实验结果表明当BA含量为4.0%～6.0%，DAAM含量为2.0%～3.0%时，乳液和膜性能较好，黏度性能较佳.用该乳液配制的胶黏剂对木材有很好的粘接性能.

Abstract

The waterborne polyurethane-acrylate hybrid emulsions modified by methyl methacrylate (MMA) and butyl acrylate (BA) copolymer were synthesized by using 1

4-butanediol (BDO)

dimethylopropionic (DMPA) and adipic dihyrazide (ADH) as chain extenders.The effects of the amounts of BA and diacetone acrylamide (DAAM) on the properties of hybrid emulsions

films and adhesive were studied.The structure of the hybrid emulsions was characterized with Fourier transform infrared (FTIR).The experiment results showed that when the amount of BA was 4.0%—6.0%

that of DAAM was 2.0%—3.0%

the properties of the hybrid emulsion

films and adhesive were satisfactory.The adhesive which was made by polyurethane-acrylate hybrid emulsion with a better adhesive for wood.

关键词

Keywords

references

浏览量

207

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

不同分子量麦草碱木素性能及其对LPF胶性能的影响

纳米铋掺杂二氧化锡/水性聚氨酯复合材料

基于Micro-CT和深度学习的盐溶液冰离心分离微观结构研究

部分预混旋流燃烧入口激励下的熵波产生及耗散机制研究

基于机器学习的改型歧管式微通道热沉流动传热特性多目标优化