- Factors influencing HDI biuret particle size coated by anionic polyacrylic hydroxyl resin
- 化工学报 2006年第1期页码：180-185
- 作者机构：
  
  1. 仲恺农业技术学院化学与化工系,广东,广州,510225
  2. 华南理工大学化学工程研究所,广东,广州,510640
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2006-01-25，
  
  纸质出版：2006-01-25
- 稿件说明：
移动端阅览
周新华, 涂伟萍, 胡剑青, 等. 影响阴离子聚丙烯酸羟基树脂包覆HDI缩二脲乳胶粒粒径的因素[J]. 化工学报, 2006,(1):180-185.

ZHOU Xinhua, TU Weiping, HU Jianqing, et al. Factors influencing HDI biuret particle size coated by anionic polyacrylic hydroxyl resin[J]. CIESC Journal, 2006, (1): 180-185.
周新华, 涂伟萍, 胡剑青, 等. 影响阴离子聚丙烯酸羟基树脂包覆HDI缩二脲乳胶粒粒径的因素[J]. 化工学报, 2006,(1):180-185. DOI：

ZHOU Xinhua, TU Weiping, HU Jianqing, et al. Factors influencing HDI biuret particle size coated by anionic polyacrylic hydroxyl resin[J]. CIESC Journal, 2006, (1): 180-185. DOI：

摘要

采用转相法制备了阴离子聚丙烯酸羟基树脂包覆HDI缩二脲乳胶粒.用TEM观察了包覆乳胶粒形态结构，分析了影响包覆乳胶粒粒径的影响因素.结果表明，乳胶粒呈现明显的核-壳结构，HDI缩二脲被聚丙烯酸羟基树脂包覆.聚丙烯酸羟基树脂分子量越大、溶剂极性越强，乳胶粒粒径越小.增加苯乙烯用量，乳胶粒粒径随之先减小后增加，苯乙烯质量分数为10%时粒径最小.乳胶粒粒径随羟基含量的增加而增大.当羟值为60 mg KOH8226;g-1时，乳胶粒粒径随着丙烯酸含量的增加而减小;当羟值在90 mg KOH8226;g-1以上时，降低丙烯酸含量有利于乳液粒径的减小.降低聚丙烯酸链间的氢键作用力，增加羟基和HDI缩二脲间的氢键作用力，能获得粒径小而均匀的包覆粒子.

Abstract

HDI biuret particle coated by anionic polyacrylic hydroxyl resin was prepared by using phase-inversion technique.The morphology of composite particle was investigated by TEM.The effects of molecule mass of polyacrylic resin

the nature of solvent

styrene(ST)content

hydroxyl value and acid value on composite particle size(D) were discussed.The result indicated that composite particle had a clear core-shell structure

with hydrophobic HDI biuret as core and acrylic resin as shell.D decreased with the increase of Mn.Using methyl amyl ketone as solvent，composite particles had bimodal particle size distribution;while using methoxypropyl acetate as solvent

composite particles had a single small particle size distribution.With the increase of ST content

D decreased first

and then increased.D reached minimum when ST content in initial monomers was 10%.D increased with the increase of hydroxyl value(HV).When HV was 60 mg KOH8226;g-1

D decreased with the increase of acid value.While HV was above 90 mg KOH8226;g-1

D increased with the increase of acid value.It was concluded that a small composite particle with narrow distribution could be obtained

by decreasing the hydrogen bond force among acrylic hydroxyl chains and increasing the hydrogen bond force between acrylic hydroxyl chain and HDI biuret.

关键词

Keywords

references

浏览量

278

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

磷酸钒锂正极材料的氮掺杂碳包覆与Ti4+共掺杂协同改性研究

稀土Y2O3基催化涂层对金属纤维表面燃烧器NO排放控制及工程验证

高速高温箔片端面密封热气弹耦合性能分析

饱和气液相密度关联外推的新通用对比态方程

基于机器学习算法的生物质热解产物产率预测研究