- Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin
- 化工学报 2005年第10期页码：2014-2018
- 作者机构：
  
  北京理工大学材料科学与工程学院,北京,100081
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 网络首发：2005-10-25，
  
  纸质出版：2005-10-25
- 稿件说明：
移动端阅览
多英全, 陈煜, 罗运军, 等. 3,4,5-三甲氧基苯甲酰-3,5-二甲基苯甲酰甲壳素的制备与表征[J]. 化工学报, 2005,(10):2014-2018.

DUO Yingquan, CHEN Yu, LUO Yunjun, et al. Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin[J]. CIESC Journal, 2005, (10): 2014-2018.
多英全, 陈煜, 罗运军, 等. 3,4,5-三甲氧基苯甲酰-3,5-二甲基苯甲酰甲壳素的制备与表征[J]. 化工学报, 2005,(10):2014-2018. DOI：

DUO Yingquan, CHEN Yu, LUO Yunjun, et al. Preparation and characterization of 3,4,5-trimethoxybenzoyl-3,5-dimethylbenzoylchitin[J]. CIESC Journal, 2005, (10): 2014-2018. DOI：

摘要

用共酰化方法制备了3

5-三甲氧基苯甲酰-3

5-二甲基苯甲酰甲壳素，获得了一类新型的具有良好溶解性能的高分子紫外线吸收剂.通过元素分析的数据计算了两种酰基的取代度，FTIR表征表明了取代反应的发生，采用X射线衍射和TG等手段对酰化产物的结晶性能和热稳定性进行了研究，通过紫外吸光度的测定计算出两种取代基的摩尔消光系数分别为9329.1 L8226;mol-18226;cm-1和652.7 L8226;mol-18226;cm-1，并对产物中的酰基进行了定量分析，结果与元素分析结果基本一致.

Abstract

5-trimethoxybenzoyl-3

5-dimethylbenzoylchitin

a kind of novel macromolecular UV absorbent with good solubility was prepared through the co-acidylating method.The substitution degree of two kinds of acyl group was calculated from the data of elemental analysis.The substitution reaction was demonstrated by the result of FTIR.The crystallinity and thermal stability of the products were studied with the methods of X-ray diffraction and TG. The molar absorptivity values of two kinds of acyl group were 9329.1 L8226;mol-18226;cm-1 and 652.7 L8226;mol-18226;cm-1 respectively

which were calculated from the data of UV absorbance.Then the acyl group content could be calculated from the UV absorbance data and the results were in agreement with those calculated from the data of elemental analysis.

关键词

Keywords

references

浏览量

161

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

射频磁控溅射法制备FC/ZnO杂化材料及其基本性质

富氧空位锌掺杂PdO/ZrO2催化CO2和苯酚合成碳酸二苯酯

微波强化焦化废盐中有机物脱除性能研究

退役光伏组件TPT背板热氧化降解特性研究

变工况下换热网络中的热量传递规律及瓶颈识别与优化