Structure and properties of continuously devulcanized ground tire rubber using independently designed single screw extruder

LÜ Xiaolong; LÜ Baiyuan; HUANG Hanxiong; JIANG Qingyan

doi:10.3969/j.issn.0438-1157.2014.11.057

您当前的位置：

首页 >

文章列表页 >

Structure and properties of continuously devulcanized ground tire rubber using independently designed single screw extruder

更新时间：2025-12-10

- Structure and properties of continuously devulcanized ground tire rubber using independently designed single screw extruder
- CIESC Journal Issue 11, Pages: 4614-4619(2014)
- 作者机构：
  
  1. 华南理工大学塑料橡胶装备及智能化研究中心,广东,广州,510640
  2. 青岛科技大学机电工程学院,山东,青岛,266061
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.11.057
  CLC： Q335+.2
- Online First：05 November 2014，
  
  Published：05 November 2014
- 稿件说明：
移动端阅览
LÜ Xiaolong, LÜ Baiyuan, HUANG Hanxiong, et al. Structure and properties of continuously devulcanized ground tire rubber using independently designed single screw extruder[J]. CIESC Journal, 2014, (11): 4614-4619.
DOI：

LÜ Xiaolong, LÜ Baiyuan, HUANG Hanxiong, et al. Structure and properties of continuously devulcanized ground tire rubber using independently designed single screw extruder[J]. CIESC Journal, 2014, (11): 4614-4619. DOI： 10.3969/j.issn.0438-1157.2014.11.057.

摘要

利用本课题组研制的单螺杆挤出机

对废旧轮胎胶(GTR)粉进行连续脱硫制备再生胶(DGTR)

并对DGTR进行再硫化制成DGTR硫化试样.结果显示

随螺杆转速增加

DGTR凝胶含量和DGTR硫化试样交联密度逐渐降低

DGTR硫化试样的拉伸强度和拉断伸长率有所提高;螺杆转速设定为40 r·min-1时

在205℃脱硫温度下取得了最好的脱硫效果

DGTR硫化试样的拉伸强度和拉断伸长率分别约为11 MPa和386%.从红外光谱和光电子能谱的分析结果推测

在单螺杆挤出机的剪切和热等的共同作用下

GTR粉中部分S—S键和C—S键发生了断裂.

Abstract

Using independently designed single screw extruder

ground tire rubber (GTR) powder was devulcanized continuously to prepare devulcanized ground tire rubber (DGTR). The DGTR was further revulcanized to prepare revulcanized DGTR samples. The gel fractions of the DGTR and the crosslink densities of the revulcanized DGTR samples decreased and the tensile strengths and elogations at break of the revulcanized DGTR samples increased gradually with increasing screw speed. The best devulcanization effectiveness was achieved under 40 r·min-1 screw speed and 205℃ devulcanization temperature. The revulcanized DGTR sample prepared under this condition exhibited tensile strength and elogation at break of about 11 MPa and 386% respectively. Inferring from the Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy analyses

parts of S—S and C—S bonds in the GTR powder were broken under both shearing and heating in the independently designed single screw extruder.

关键词

Keywords

references

Views

444

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Synthesis and characterization of cationic starch dye adsorbing material

Absorption performance of CO2 in amino-functionalized task-specific ionic liquids

UV photocatalysis-assisted adsorptive desulfurization of gasoline using bi-functional Ti-Si-O material

Zn3-MOF as highly efficient fluorescent sensor for nitrobenzene

Preparation of DMAPS-modified PVDF membranes via pre-radiation-induced graft polymerization for effective oil/water emulsion separation

Related Author

WANG Jiankun

GUO Jing

ZHANG Hao

FAN Xinyu

LIANG Ka

ZHANG Hui

ZHANG Hongmei

SHEN Jinyou

Related Institution

College of Textile, Tianjin University of Technology

Jiangsu Collaborative Innovation Center of Atmospheric Environment and Equipment Technology(CICAEET), Jiangsu Key Laboratory of Atmospheric Environment Monitoring & Pollution Control, Nanjing University of Information Science & Technology

School of Environmental and Biological Engineering, Nanjing University of Science and Technology

School of Chemistry and Chemical Engineering, South China University of Technology

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology

⁰