Waterborne polyurethane adhesive modified by epoxy oil soybean and 3-aminopropyltriethoxysilane

更新时间：2025-12-10

- Waterborne polyurethane adhesive modified by epoxy oil soybean and 3-aminopropyltriethoxysilane
- CIESC Journal Issue 11, Pages: 4599-4606(2014)
- 作者机构：
  
  华南理工大学化学与化工学院,广东,广州,510640
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.11.055
  CLC： Q323.8
- Online First：05 November 2014，
  
  Published：05 November 2014
- 稿件说明：
移动端阅览
HE Feiqiang, FU Heqing, ZHOU Wei. Waterborne polyurethane adhesive modified by epoxy oil soybean and 3-aminopropyltriethoxysilane[J]. CIESC Journal, 2014, (11): 4599-4606.
DOI：

HE Feiqiang, FU Heqing, ZHOU Wei. Waterborne polyurethane adhesive modified by epoxy oil soybean and 3-aminopropyltriethoxysilane[J]. CIESC Journal, 2014, (11): 4599-4606. DOI： 10.3969/j.issn.0438-1157.2014.11.055.

摘要

以环氧大豆油(ESO)与3-氨基丙基三乙氧基硅烷(KH550)双重交联改性水性聚氨酯(WPU).通过FTIR、TG、DSC、DMA、AFM、粒径分析仪、拉力试验机等仪器对改性的水性聚氨酯进行了表征.研究了ESO和KH550的含量对水性聚氨酯乳液、胶膜以及胶黏剂性能的影响.分析了KH550对水性聚氨酯结晶性能和微相分离的影响.研究发现

随着ESO与KH550的加入

水性聚氨酯乳液的性能得到改善

胶膜的吸水率先减小后增大

拉伸强度逐渐增大

断裂伸张率逐渐减小.水性聚氨酯胶黏剂对PVC的T-剥离强度先增大后减小.随着KH550含量的增加

热稳定性逐步改善

结晶性降低

软段与硬段相混合程度提高.当ESO为4%、KH550为2%(均为质量分数)时

水性聚氨酯胶黏剂的综合性能最好.

Abstract

Waterborne polyurethane (WPU) modified by epoxy soybean oil (ESO) and 3-aminopropyltriethoxysilane (KH550) were synthesized. The properties of the modified WPU were characterized by FTIR

DSC

DMA

AFM

particle size analyzer and tensile test machine. The effects of contents of ESO and KH550 on the properties of WPU emulsion

its film and adhesive strength were studied. And the effect of KH550 on the crystallinity and microphase separation of WPU was analyzed. With the increase of contents of ESO and KH550

the properties of WPU dispersion were improved

the water absorption of WPU film decreased first

and then increased. Tensile strength increased

while elongation at break decreased. The T-peel strength of the adhesive to PVC/PVC increased first

and then decreased. With increasing KH550 content

thermal stability of the WPU film was improved

crystallinity decreased

degree of mixing of soft segment phase and hard segment phase was enhanced. When the contents of ESO and KH550 were 4% and 2%(mass)

respectively

the properties of WPU adhesive were perfect.

关键词

Keywords

references

Views

508

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of HDI/IPDI mole ratio on properties of waterborne polyurethane and its film

Facile preparation and properties of chemically modified galactomannan films via mild hydroxy-alkyne click reaction

Study on boiling characteristics of liquid crystal elastomer surfaces with thermally adaptive wettability

Numerical study on damage behavior of rubber O-ring seals under hydrogen-friction coupling effects

Research progress on modification strategies and applications of water-based binders for lithium-ion batteries

Related Author

颜财彬

LIU Haiqin

LI Bowen

LING Zhe

LIU Liang

YU Juan

FAN Yimin

YONG Qiang

Related Institution

华南理工大学化学与化工学院

College of Chemical Engineering, Nanjing Forestry University

School of Energy Science Engineering, Harbin Institute of Technology

Suzhou Research Institute, Harbin Institute of Technology

School of Mechanical and Automotive Engineering, South China University of Technology

⁰