Synthesis of poly(vinyl chloride)-butyl acrylate graft copolymer by ARGET ATRP method

LIU Keyong; BAO Yongzhong

doi:10.3969/j.issn.0438-1157.2014.08.056

您当前的位置：

首页 >

文章列表页 >

Synthesis of poly(vinyl chloride)-butyl acrylate graft copolymer by ARGET ATRP method

更新时间：2025-12-10

- Synthesis of poly(vinyl chloride)-butyl acrylate graft copolymer by ARGET ATRP method
- CIESC Journal Issue 8, Pages: 3261-3267(2014)
- 作者机构：
  
  浙江大学化学工程与生物工程学系, 化学工程联合国家重点实验室,浙江,杭州,310027
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.08.056
  CLC： Q325.3
- Online First：05 August 2014，
  
  Published：05 August 2014
- 稿件说明：
移动端阅览
LIU Keyong, BAO Yongzhong. Synthesis of poly(vinyl chloride)-butyl acrylate graft copolymer by ARGET ATRP method[J]. CIESC Journal, 2014, (8): 3261-3267.
DOI：

LIU Keyong, BAO Yongzhong. Synthesis of poly(vinyl chloride)-butyl acrylate graft copolymer by ARGET ATRP method[J]. CIESC Journal, 2014, (8): 3261-3267. DOI： 10.3969/j.issn.0438-1157.2014.08.056.

摘要

以不稳定氯含量高的聚氯乙烯（U-PVC）和氯乙烯-溴代异丁酸烯丙酯共聚物（PVC-co-ABrMP）为大分子引发剂，使用电子转移催化再生原子转移自由基聚合（ARGET ATRP）进行丙烯酸丁酯（BA）的溶液接枝共聚。在固定CuCl2：三（2-吡啶甲基）胺：辛酸亚锡（摩尔比）时，当CuCl2用量（相对于氯乙烯链节数）小于0.1%时，BA转化率随CuCl2用量增加而明显增加；辛酸亚锡与CuCl2摩尔比大于50时，辛酸亚锡用量对聚合速率的影响较小；相同催化体系用量下，采用PVC-co-ABrMP为引发剂，可获得更高的BA转化率。通过PVC-co-ABrMP酯基水解得到PBA支链，其分子量分布指数为1.29，符合“活性”自由基聚合的特征。接枝PBA对PVC有明显的内增塑效果，PBA摩尔分数为32.75%的PVC-g-BA的玻璃化温度为8.34℃。

Abstract

The grafting copolymerization of butyl acrylate (BA) onto poly(vinyl chloride) (PVC) was conducted through the method of activators regenerated by electron transfer atom transfer radical polymerization (ARGET ATRP)

using PVC with higher labile chlorine content (U-PVC) and vinyl chloride/allyl 2-bromo-2-methylpropionate random copolymer (PVC-co-ABrMP) as an initiator. The polymerization conversion of BA was obviously increased as CuCl2 concentration (based on number of vinyl chloride unit) increased when CuCl2 concentration was lower than 0.1%. The increase of BA polymerization rate was not obvious when Sn(EH)2/CuCl2 molar ratio exceeded 50. The greater BA polymerization rate and PBA grafting degree were achieved when PVC-co-ABrMP was used as the initiator with the same catalyst. The side PBA chains were cleaved from the ester group of PVC-co-ABrMP and the molecular weight distribution index of PBA was 1.29

verifying the “living” nature of this graft copolymerization. The grafted PBA showed good internal plasticization effect on PVC

and the glass temperature of PVC-g-BA copolymer with 32.75%(mol) PBA was reduced to 8.34℃.

关键词

Keywords

references

Views

461

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Synthesis of a high-efficacy medium-entropy alloy catalyst via the recycling of spent batteries and its subsequent performance evaluation

Advances in nickel catalyzed controlled/living radical polymerization reactions

Dielectric properties of mixed materials in transesterification reaction system

Preparation and performance evaluation of Ni2P/SiO2 catalysts for acetic acid hydrogenation to produce ethanol

Synthesis of syndiotactic-rich polystyrene with neodymium-based catalyst

Related Author

GUO Shan

TIAN Yu

XU Yongbin

WANG Peng

LIU Zhiming

CHENG Xiaokai

LI Wei

WANG Jingdai

Related Institution

College of Electromechanical Engineering, Qingdao University of Science & Technology

Ningbo Innovation Center, Zhejiang University

College of Chemical &Biological Engineering, Zhejiang University

School of Mechanical Engineering, Jiangnan University, Jiangsu Key Laboratory of Advanced Food Manufactoring Equipment and Technology

College of Chemical Engineering, Zhejiang University of Technology

⁰