CO chemical looping combustion using Co-Fe2O3 nano oxygen carrier for enrichment of CO2

QIN Wu; LI Qu; DONG Changqing; CHENG Weiliang; YANG Yongping

doi:10.3969/j.issn.0438-1157.2014.08.039

您当前的位置：

首页 >

文章列表页 >

CO chemical looping combustion using Co-Fe₂O₃ nano oxygen carrier for enrichment of CO₂

更新时间：2025-12-10

- CO chemical looping combustion using Co-Fe₂O₃ nano oxygen carrier for enrichment of CO₂
- CIESC Journal Issue 8, Pages: 3136-3143(2014)
- 作者机构：
  
  华北电力大学生物质发电成套设备国家工程实验室,北京,102206
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.08.039
  CLC： K16
- Online First：05 August 2014，
  
  Published：05 August 2014
- 稿件说明：
移动端阅览
QIN Wu, LI Qu, DONG Changqing, et al. CO chemical looping combustion using Co-Fe₂O₃ nano oxygen carrier for enrichment of CO₂[J]. CIESC Journal, 2014, (8): 3136-3143. DOI: 10.3969/j.issn.0438-1157.2014.08.039.
DOI：

QIN Wu, LI Qu, DONG Changqing, et al. CO chemical looping combustion using Co-Fe₂O₃ nano oxygen carrier for enrichment of CO₂[J]. CIESC Journal, 2014, (8): 3136-3143. DOI: 10.3969/j.issn.0438-1157.2014.08.039. DOI：

摘要

制备了不同量级Co掺杂Fe2O3载氧体Co-Fe2O3，利用BET和TEM对载氧体结构进行表征。通过在不同温度下Co-Fe2O3与气体燃料CO的还原反应，考察Co-Fe2O3对CO化学链燃烧特性。结果表明，同一温度条件下，掺杂量越高，还原反应转化率越高；掺杂量不变的情况下，温度升高促使还原程度加深，缩短了载氧体完全还原转化的时间。根据TGA曲线进行了化学动力学分析，发现Co0.2Fe还原反应过程在344.7～391.0℃和414.7～472.5℃温度范围反应动力学对应扩散控制的Jander方程模型，607.6～681.5℃温度范围对应二维扩散反应模型，并分别计算出相应模型的表观活化能和频率因子。结果可为化学链燃烧技术应用提供理论指导。

Abstract

Co-doped Fe2O3 of different orders of magnitude were prepared as oxygen carriers

the structures of which were characterized with adsorption-desorption (BET) and transmission electron microscope (TEM). Experiments under different temperatures were performed to investigate the reaction between Co-doped Fe2O3 and CO to understand the chemical looping combustion characteristics of these prepared oxygen carriers. The higher the doping amount

the higher the reduction conversion at the same temperature. However

with the same doping amount

increase of temperature led to increase of reduction degree

shortening the time of complete conversion of oxygen carrier. Further analysis of chemical kinetics and reaction dynamics based on TGA curve showed that the Jander equation model was suitable for the reduction of Co-doped Fe2O3 at 344.7-391.0℃ and 414.7-472.5℃

and the Valensi equation model was suitable for the reduction at 607.6-681.5℃

according to which the kinetic parameters including activation energy and pre-exponential factor were also calculated. The research results could provide theoretical guidance for further application of CLC technology.

关键词

Keywords

references

Views

501

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

The analysis of energy efficiency for TVSA-based direct air capture system

Metal-organic framework encapsulating carbon nanotubes for trace CO2 separation

Morphology regulation of BiOBr and study on its performance of photocatalytic CO2 reduction

CO working capacity and operating conditions of Co-MOF-74 and Mg-MOF-74

Experimental study on cyclic heat storage performance of TiO2-doped calcium based materials under pressurized carbonation

Related Author

LIU Shaonan

WU Junye

WANG Kuihua

LI Qian

CHEN Yunhao

GE Tianshu

LIU Wenchuan

ZENG Zilong

Related Institution

Institute of Refrigeration and Cryogenics, Shanghai Jiao Tong University

State Key Laboratory of Multiphase Flow in Power Engineering, Xi’an Jiaotong University

College of Mechanical Engineering, Xi’an Shiyou University

School of Chemistry and Chemical Engineering, Guangxi University

Institute of Green Petroleum Processing and Light Hydrocarbon Conversion, College of Chemical Engineering, Zhejiang University of Technology

⁰