Preparation and adsorption behavior of Cu(Ⅱ) ion-imprinted composite membranes via electrostatic assembly

FAN Rongyu; ZHENG Ximing; LIN Xing

doi:10.3969/j.issn.0438-1157.2014.08.027

您当前的位置：

首页 >

文章列表页 >

Preparation and adsorption behavior of Cu(Ⅱ) ion-imprinted composite membranes via electrostatic assembly

更新时间：2025-12-10

- Preparation and adsorption behavior of Cu(Ⅱ) ion-imprinted composite membranes via electrostatic assembly
- CIESC Journal Issue 8, Pages: 3039-3047(2014)
- 作者机构：
  
  绿色化工技术福建省高等学校重点实验室, 武夷学院生态与资源工程学院, 福建武夷山,354300
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.08.027
  CLC： 63TQ028.8
- Online First：05 August 2014，
  
  Published：05 August 2014
- 稿件说明：
移动端阅览
FAN Rongyu, ZHENG Ximing, LIN Xing. Preparation and adsorption behavior of Cu(Ⅱ) ion-imprinted composite membranes via electrostatic assembly[J]. CIESC Journal, 2014, (8): 3039-3047.
DOI：

FAN Rongyu, ZHENG Ximing, LIN Xing. Preparation and adsorption behavior of Cu(Ⅱ) ion-imprinted composite membranes via electrostatic assembly[J]. CIESC Journal, 2014, (8): 3039-3047. DOI： 10.3969/j.issn.0438-1157.2014.08.027.

摘要

将聚丙烯酸和聚亚乙基亚胺-Cu（Ⅱ）络合物通过静电作用交替组装到聚丙烯微孔膜（MPPM）表面，再通过环氧氯丙烷的交联，使组装层形成交联体系，洗脱除去Cu（Ⅱ）离子，制得Cu（Ⅱ）离子印迹复合膜。采用FTIR、XPS和ESEM对膜表面的化学组成及物理形态进行了表征。制得的离子印迹复合膜具有良好的亲水性和稳定性，吸水量能够达到MPPM的819倍以上；在1.5 mol·L-1 的NaCl水溶液或55℃水浴中振荡洗涤48 h，膜表面的组装层质量能保持在94%以上。平衡吸附实验结果发现，离子印迹复合膜对Cu（Ⅱ）离子具有良好的吸附能力与高的选择性，饱和吸附量可达112.87 mg·cm-2，以Pb（Ⅱ）、Zn（Ⅱ）、Ni（Ⅱ）、Co（Ⅱ）、Mg（Ⅱ）或Mn（Ⅱ）作为竞争离子，膜对Cu（Ⅱ）离子的选择性系数分别达17.72、26.66、17.43、16.87、29.72和19.75。吸附热力学与动力学研究结果表明，吸附属于单分子层吸附，吸附主要受化学作用控制。制得的离子印迹复合膜具有良好的再生能力，10次吸附-脱附循环后，对Cu（Ⅱ）离子的吸附量能保持在90%以上。

Abstract

The layer-by-layer electrostatic assembly process and chemical cross-linking technology were developed for Cu(Ⅱ) ion-imprinted composite membranes. Poly(acrylic acid) and polyethylenimine-copper(Ⅱ) ion complexes were assembled alternately on the surface of microporous polypropylene membrane (MPPM) by electrostatic action. Then the assembled layers were cross-linked by epichlorohydrin. The Cu(Ⅱ)-ion imprinted composite membranes obtained after the removal of Cu(Ⅱ) ions with acetic acid

characterized by Fourier transform infrared spectroscopy

X-ray photoelectron spectroscopy and environmental scanning electron microscopy

show satisfactory hydrophilicity and stability. The composite membrane can take water up to 819 times that of MPPM. The mass of assembled layers can maintain more than 94% after oscillating washing in 1.5 mol·L-1 NaCl solution or in 55℃ water for 48 h. The equilibrium adsorption experiments indicate that the ion-imprinted composite membranes exhibit high adsorption capability and high selectivity towards Cu(Ⅱ). The maximum adsorption capacity is 112.87 mg·cm-2

and the selectivity coefficients are 17.72

26.66

17.43

16.87

29.72 and 19.75 with Pb(Ⅱ)

Zn(Ⅱ)

Ni(Ⅱ)

Co(Ⅱ)

Mg(Ⅱ) and Mn(Ⅱ) as competing ions

respectively. The adsorption thermodynamics and kinetics show that the adsorption process of Cu(Ⅱ) is in monolayer adsorption and is dominated by chemical interaction. The ion-imprinted composite membranes exhibit good regeneration ability

and their adsorption capacity can be maintained over 90% even after ten adsorption-desorption cycles.

关键词

Keywords

references

Views

393

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Vapor-phase synthesis and post-synthetic modification of metal-organic framework membranes

Hydrophobic pervaporation membranes on polymer substrate for solvent recovery

Progress in isolating lithium resources from China salt lake brine

Recent progress of membrane materials for mono-/di-valent ions separation

Optimized fabrication of mixed matrix membranes based on amino-MIL-101(Cr) for highly efficient CO2 separation

Related Author

ZHANG Yaohui

BAN Yujie

YANG Weishen

XU Zehai

LIU Chao

ZHANG Guoliang

Chenxiao JIANG

Binglun CHEN

Related Institution

State Key Laboratory of Catalysis,Dalian Institute of Chemical Physics, Chinese Academy of Science

University of Chinese Academy of Sciences

Center for Membrane and Water Science &Technology, Collaborative Innovation Center of Membrane Separation and Water Treatment of Zhejiang Province, Zhejiang University of Technology

School of Chemistry and Materials Science, University of Science and Technology of China

State Key Laboratory of Materials-Oriented Chemical Engineering, College of Chemical Engineering, Nanjing Tech University

⁰