Preparation and gas separation performance of hydrophobic SiO<sub>2</sub>/PTFPMS hybrid composite membrane

NIE Fei; HE Gaohong; ZHAO Wei; JU Jia; LI Hao

doi:10.3969/j.issn.0438-1157.2014.08.024

您当前的位置：

首页 >

文章列表页 >

Preparation and gas separation performance of hydrophobic SiO₂/PTFPMS hybrid composite membrane

更新时间：2025-12-10

- Preparation and gas separation performance of hydrophobic SiO₂/PTFPMS hybrid composite membrane
- CIESC Journal Issue 8, (2014)
- 作者机构：
  
  1. 大连理工大学化工学院,辽宁,大连,116024
  2. 沈阳化工大学石油化工学院,辽宁,辽阳,111003
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.08.024
  CLC： Q028.8
- Online First：05 August 2014，
  
  Published：05 August 2014
- 稿件说明：
移动端阅览
NIE Fei, HE Gaohong, ZHAO Wei, et al. Preparation and gas separation performance of hydrophobic SiO₂/PTFPMS hybrid composite membrane[J]. CIESC Journal, 2014, (8). DOI: 10.3969/j.issn.0438-1157.2014.08.024.
DOI：

NIE Fei, HE Gaohong, ZHAO Wei, et al. Preparation and gas separation performance of hydrophobic SiO₂/PTFPMS hybrid composite membrane[J]. CIESC Journal, 2014, (8). DOI: 10.3969/j.issn.0438-1157.2014.08.024. DOI：

摘要

为了提高气体分离膜的耐溶胀特性，以多孔聚醚酰亚胺（PEI）为支撑层，采用溶液共混法制备了疏水SiO2/PTFPMS杂化复合膜，研究了疏水SiO2质量共混比对膜形态、耐溶胀性以及不同操作压差下的纯气渗透分离性能的影响。光学显微照片显示，当共混比不超过0.018时，杂化膜的透明度较高，表明疏水SiO2与PTFPMS具有较好的相容性；当SiO2与PTFPMS的共混比超过0.018时，SiO2团聚明显。SEM表征结果显示，杂化膜表面光洁，断面杂化涂层紧密贴合支撑层。疏水SiO2/PTFPMS杂化膜在异辛烷中的溶胀度为0，在乙酸乙酯中的溶胀度比PTFPMS均质膜的下降了11.9%，显示了其优异的耐溶胀性能。在操作压力为1.0 MPa，操作温度为25℃下，SiO2共混比为0.012时，疏水SiO2/PTFPMS杂化复合膜的CO2渗透通量达到最高156.1GPU，CO2/N2选择性为15.86。

Abstract

To improve the solvent resistance property of gas separation membrane

a hydrophobic SiO2/polytrifluoropropylsiloxane (PTFPMS) hybrid composite membrane was fabricated on a porous polyetherimide (PEI) support with solution blending method. The effects of mass ratio of hydrophobic SiO2 to PTFPMS on the membrane morphology

solvent resistance

and gas separation performance of the hydrophobic SiO2/PTFPMS hybrid composite membrane were investigated. The optical microscope images show good miscibility between SiO2 and PTFPMS with the increase of blend ratio till 0.018. At blend ratios higher than 0.018

SiO2 particles exhibit obvious aggregation in the hybrid membrane. SEM images show that no obvious defect is on the surface of the SiO2/PTFPMS selective layer that is closely stuck on the PEI support. The swelling degree of the hydrophobic SiO2/PTFPMS hybrid homogeneous film is 0 in nonpolar solvent octane and is declined by 11.9% in polar solvent ethyl acetate compared with PTFPMS homogeneous film

indicating the improved solvent resistance of the SiO2/PTFPMS hybrid homogeneous film. The CO2 gas permeation rate can reach as high as 156.1 GPU and the selectivity of CO2/N2 is 15.86 when the blend ratio of SiO2 is 0.012 under the transmembrane pressure difference up to 1.0 MPa.

关键词

Keywords

references

Views

892

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Fabrication of boron-doped hybrid silica membranes for pervaporation desalination

Research of thin film nanocomposite (TFN) membranes incorporated spherical mesoporous silica nanoparticles with carboxyl group

Fabrication of PVDF-SiO2/PVSQ superhydrophobic compositemembrane via self-assembly with anti-fouling property for membrane distillation

Properties of bagasse nano-cellulose by alkaline hydrolysis/styrene butadiene rubber composite

Preparation of free-standing graphene carbon membrane for gas separation

Related Author

Rui ZHANG

Qi SHAO

Huayu ZHANG

Zelong JIN

Xiaoliang ZHANG

Yan SUN

Shitao LIU

Shang DENG

Related Institution

College of Chemistry and Chemical Engineering, Jiangxi Normal University

Kunshan Innovation Institute of Nanjing University, Kunshan

College of Life Sciences and Technology, Heilongjiang Bayi Agricultural University

State Key Laboratory of Urban Water Resource and Environment, School of Environmental, Harbin Institute of Technology

School of Chemistry and Environmental Engineering, Harbin University of Science and Technology

⁰

Preparation and gas separation performance of hydrophobic SiO2/PTFPMS hybrid composite membrane

DOI：10.3969/j.issn.0438-1157.2014.08.024

摘要

Abstract

关键词

Keywords

references

Preparation and gas separation performance of hydrophobic SiO₂/PTFPMS hybrid composite membrane