Extracting magnesium from ascharite by vacuum thermal reduction using calcium carbide as redutant

WANG Yaowu; PENG Jianping; LI Yinglong; ZHAO Kun; SONG Yang; FENG Naixiang

doi:10.3969/j.issn.0438-1157.2014.06.025

您当前的位置：

首页 >

文章列表页 >

Extracting magnesium from ascharite by vacuum thermal reduction using calcium carbide as redutant

更新时间：2025-12-10

- Extracting magnesium from ascharite by vacuum thermal reduction using calcium carbide as redutant
- CIESC Journal Issue 6, Pages: 2130-2136(2014)
- 作者机构：
  
  东北大学材料与冶金学院,辽宁,沈阳,110004
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.06.025
  CLC： F131.1
- Online First：05 June 2014，
  
  Published：05 June 2014
- 稿件说明：
移动端阅览
WANG Yaowu, PENG Jianping, LI Yinglong, et al. Extracting magnesium from ascharite by vacuum thermal reduction using calcium carbide as redutant[J]. CIESC Journal, 2014, (6): 2130-2136.
DOI：

WANG Yaowu, PENG Jianping, LI Yinglong, et al. Extracting magnesium from ascharite by vacuum thermal reduction using calcium carbide as redutant[J]. CIESC Journal, 2014, (6): 2130-2136. DOI： 10.3969/j.issn.0438-1157.2014.06.025.

摘要

对以硼镁石为原料，以碳化钙为还原剂的真空热还原炼镁以实现硼镁分离进行了研究，通过对煅烧后的物料进行物相分析，对碳化钙还原硼镁石过程中氧化镁还原率较低的原因进行了分析，并对还原过程中影响氧化镁还原率的因素进行了探讨。研究结果表明：以硼镁石为原料进行煅烧后获得的煅后硼镁石的氧化镁主要以硼酸镁和硅酸镁化合物的形式存在，游离的氧化镁较少是导致还原过程中氧化镁还原率较低的主要原因。在煅烧过程中添加氧化钙可使以化合物形式存在的氧化镁游离出来大幅增加氧化镁的还原率。在煅烧过程中配入氧化钙后进行真空热还原炼镁可有效实现硼镁石中的硼镁分离，其还原过程中的氧化镁还原率可达85%以上，还原后获得的还原渣主要物相为CaO和3CaO·B2O3，可作为生产无碱玻璃纤维的原料，能够实现硼镁石的综合利用。

Abstract

A method separating magnesium and boron from ascharite by vacuum thermal reduction using calcium carbide as redutant was studied experimentally. The reason that led to low reduction ratio of MgO in the vacuum thermal reduction process was researched by phase analysis of calcined ascharite and the influencing factors were analyzed. The results show that magnesium in the calcined ascharite is mainly involved in magnesium borate and magnesium silicate

reduction of which is difficult and only small amount is free state of MgO

which is the main cause of low reduction ratio. The addition of CaO during calcination of ascharite can promote formation of more free state MgO and reduction of more MgO. As long as enough CaO is added

magnesium and boron can be effectively separated and reduction rate can be over 85%. The main phases in reduction slag are CaO and 3CaO·B2O3. The reduction slag can be used as raw material for production of alkali free glass fiber. So the comprehensive utilization of ascharite ore can be realized.

关键词

Keywords

references

Views

298

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Reductive removing selenium from electrolytic manganese anolytewith iron powder

Research progress of ionic liquids in separation of aromatics/alkanes and olefins/alkanes

A hybrid modeling and optimization strategy for sequential simulated moving bed

Mixed matrix membranes based on nitrogen-rich Schiff base network polymer and their CO2 separation performance

Study on flash evaporation characteristics as well as thermodynamic variation performance in liquid hydrogen tank during on-orbit venting

Related Author

WANG Yuhong

LÜ Yan

NONG Jingyi

LAN Ziliu

JIANG Jialuan

SU Haifeng

YIN Mengfan

DENG Kaixin

Related Institution

Guangxi Colleges and Universities Key Laboratory of New Technology and Application in Resource Chemical Engineering, School of Chemistry and Chemical Engineering, Guangxi University

State Key Laboratory of Heavy Oil Processing, China University of Petroleum

Key Laboratory of Advanced Control for Light Industry Process of the Ministry of Education, Jiangnan University

College of Chemistry and Chemical Engineering, Taiyuan University of Technology

Shanxi Key Laboratory of Gas Energy Efficient and Clean Utilization

⁰