Polystyrene /TiO<sub>2</sub> nanotubes composite microspheres fabricated via Pickering emulsion polymerization stabilized by TiO<sub>2</sub> nanotubes

ZHANG Fang; SHI Tiejun; ZHOU Xun; ZHOU Hai'ou; WU Jing

doi:10.3969/j.issn.0438-1157.2014.04.050

您当前的位置：

首页 >

文章列表页 >

Polystyrene /TiO₂ nanotubes composite microspheres fabricated via Pickering emulsion polymerization stabilized by TiO₂ nanotubes

更新时间：2025-12-10

- Polystyrene /TiO₂ nanotubes composite microspheres fabricated via Pickering emulsion polymerization stabilized by TiO₂ nanotubes
- CIESC Journal Issue 4, Pages: 1526-1530(2014)
- 作者机构：
  
  合肥工业大学化工学院,安徽,合肥,230009
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.04.050
  CLC： 631
- Online First：27 November 2013，
  
  Published：27 November 2013
- 稿件说明：
移动端阅览
ZHANG Fang, SHI Tiejun, ZHOU Xun, et al. Polystyrene /TiO₂ nanotubes composite microspheres fabricated via Pickering emulsion polymerization stabilized by TiO₂ nanotubes[J]. CIESC Journal, 2014, (4): 1526-1530. DOI: 10.3969/j.issn.0438-1157.2014.04.050.
DOI：

ZHANG Fang, SHI Tiejun, ZHOU Xun, et al. Polystyrene /TiO₂ nanotubes composite microspheres fabricated via Pickering emulsion polymerization stabilized by TiO₂ nanotubes[J]. CIESC Journal, 2014, (4): 1526-1530. DOI: 10.3969/j.issn.0438-1157.2014.04.050. DOI：

摘要

利用γ-甲基丙烯酰氧基丙基三甲氧基硅烷（KH-570），对水热法制备的TiO2纳米管进行了表面改性，并用改性的纳米管为稳定剂，采用Pickering乳液聚合法制备了聚苯乙烯/TiO2纳米管复合微球。采用红外光谱（IR）、光学显微镜、高分辨透射电镜（HRTEM）、高分辨扫描电子显微镜（FESEM）、X射线光电子能谱（XPS）等分析手段，对改性前后TiO2纳米管以及复合微球的结构和形貌进行了表征，用三相接触角仪测试并优化了TiO2纳米管的表面润湿性。研究结果表明，当mKH-570/mTiO2=15%时，改性TiO2纳米管表面润湿性最佳，能很好地稳定Pickering乳液聚合，聚合后可以得到壳层为致密均匀TiO2纳米管，核为聚苯乙烯的复合微球。

Abstract

TiO2 nanotube prepared via the hydrothermal method was modified with KH-570 and then the modified TiO2 nanotube was used as an emulsifier to fabricate PS/TiO2 nanotube composite microspheres via Pickering emulsion polymerization. The TiO2 nanotubes and composite microspheres were characterized by IR

optical microscope

HRTEM

FESEM and XPS. The surface wettability of TiO2 was measured with contact angle meter. When the value of mKH-570/mTiO2 was 0.15

the modified TiO2 nanotube possessed the best surface wettability and it could satisfactorily stabilize the St-in-water Pickering emulsion polymerization. And then the composite microspheres with PS nucleus and dense

homogeneous TiO2 nanotubes shells could be obtained via Pickering emulsion polymerization.

关键词

Keywords

references

Views

804

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Biosynthesis of chiral epichlorohydrin by halohydrin dehalogenase based on Pickering emulsion system

Preparation and characterization of paraffin Pickering emulsion without subcooling phenomenon

Preparation and modulation of Pickering emulsion stabilized by non-covalent hydrophobic modified nanoparticles

E@Alg@s-TiO2 microsphere stabilized O/W Pickering emulsion and the enhancement of interfacial enzymatic catalysis

Preparation of TiO2/attapulgite composite photocatalyst by supercritical fluid drying method

Related Author

TANG Xiaoling

WANG Jiarui

ZHU Xuanye

ZHENG Renchao

Shaoqing RU

Yafei WU

Liming CHE

Dongqin LUO

Related Institution

College of Bioengineering, Zhejiang University of Technology

College of Chemistry and Chemical Engineering, Xiamen University

Shenzhen Minshun Primary School

Shandong Linglong Tire Co., Ltd., Zhaoyuan

School of Materials Science and Engineering

⁰

Polystyrene /TiO2 nanotubes composite microspheres fabricated via Pickering emulsion polymerization stabilized by TiO2 nanotubes

DOI：10.3969/j.issn.0438-1157.2014.04.050

摘要

Abstract

关键词

Keywords

references

Polystyrene /TiO₂ nanotubes composite microspheres fabricated via Pickering emulsion polymerization stabilized by TiO₂ nanotubes