Preparation of ternary composite Ca-based material CaO-Ca3Al2O6-MgO for high-temperature CO2 capture

ZHANG Mingming; PENG Yunxiang; WANG Jin; LI Ping; YU Jianguo

doi:10.3969/j.issn.0438-1157.2014.01.029

您当前的位置：

首页 >

文章列表页 >

Preparation of ternary composite Ca-based material CaO-Ca₃Al₂O₆-MgO for high-temperature CO₂ capture

更新时间：2025-12-10

- Preparation of ternary composite Ca-based material CaO-Ca₃Al₂O₆-MgO for high-temperature CO₂ capture
- CIESC Journal Issue 1, Pages: 227-236(2014)
- 作者机构：
  
  华东理工大学化学工程联合国家重点实验室,上海,200237
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.01.029
  CLC： Q028.1+5
- Online First：05 January 2014，
  
  Published：05 January 2014
- 稿件说明：
移动端阅览
ZHANG Mingming, PENG Yunxiang, WANG Jin, et al. Preparation of ternary composite Ca-based material CaO-Ca₃Al₂O₆-MgO for high-temperature CO₂ capture[J]. CIESC Journal, 2014, (1): 227-236. DOI: 10.3969/j.issn.0438-1157.2014.01.029.
DOI：

ZHANG Mingming, PENG Yunxiang, WANG Jin, et al. Preparation of ternary composite Ca-based material CaO-Ca₃Al₂O₆-MgO for high-temperature CO₂ capture[J]. CIESC Journal, 2014, (1): 227-236. DOI: 10.3969/j.issn.0438-1157.2014.01.029. DOI：

摘要

采用Al2O3和MgO同时掺杂改性的方法制备了CaO-Ca3Al2O6-MgO复合钙基高温吸附CO2材料。复合钙基材料孔隙发达，活性物相为CaO，惰性骨架物相为Ca3Al2O6和MgO。Ca3Al2O6/MgO质量比偏小的材料，表面微粒粒径较小。在10%（体积分数，下同）CO2和90% N2的混合气气氛下，采用热重分析仪测量了复合钙基材料吸附CO2容量、碳化反应速率以及循环碳化（670℃）/煅烧（900℃）过程的稳定性。结果发现，复合钙基材料CaO-Ca3Al2O6-MgO具有较好的吸附CO2性能，提高Ca3Al2O6/MgO质量比，合成材料的循环稳定性较好；降低Ca3Al2O6/MgO质量比，合成材料的碳化反应速率加快，CaO转化率提高。最后，通过对不同循环次数下复合钙材料的比表面积、孔径分布、微观形貌、表面元素分布，晶相、晶粒大小进行研究分析，对合成材料的失活以及掺杂物质对烧结的抑制机理进行了讨论。

Abstract

Synthetic sintering-resistant calcium based material for high-temperature CO2 capture was prepared by doping Al2O3 and MgO into CaO using wet chemical method. The synthetic materials with pore structure developed consist of three substances

CaO

Ca3Al2O6 and MgO. Lower mass ratio of Ca3Al2O6/MgO gives smaller grain size of the synthetic material. CO2 capture capacities and cyclic carbonation/calcination (670/900℃) stability were evaluated in thermogravimetric analyzer under the simulated 10%(vol.

the same below) CO2 (90% N2). It is found that the synthetic CaO-Ca3Al2O6-MgO material presents good performance to capture CO2 from the flue gas

and the mass ratio of Ca3Al2O6/MgO has significant effect on CO2 capture performance. Lower mass ratio leads to faster carbonation reaction rate and higher CaO conversion. Moreover

the deactivation mechanism of synthetic material and the anti-sintering mechanism of doping agents were studied through analysis of specific surface area

pore volume

micro morphology

element distribution

phase composition and grain size of CaO-Ca3Al2O6-MgO material after multicycle carbonation/calcination.

关键词

Keywords

references

Views

725

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Modulation of nano CaCO3 pore size and effect on properties of carbonation reaction

Zn-doped PdO/ZrO2 with rich oxygen vacancies for the synthesis of diphenyl carbonate from CO2 and phenol

Research progress in electrocatalytic synthesis of urea from carbon dioxide and nitrate

Construction of Ni-N co-doped carbon aerogel and its performance in electrocatalytic reduction of CO2

Experimental investigation on solubility of CO2 in two dipentaerythritol esters

Related Author

LU Shangqing

WU Sufang

XING Mengke

ZHENG Tao

HUI Tianli

MENG Xianghai

ZHANG Rui

LIU Haiyan

Related Institution

College of Chemical and Biological Engineering, Zhejiang University

State Key Laboratory of Heavy Oil Processing, China University of Petroleum

College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Shanxi Key Laboratory of Efficient and Clean Utilization of Gas Energy

Shanxi Research Institute of Huairou Laboratory

School of Chemistry and Chemical Engineering, Anhui Province Key Laboratory of Coal Clean Conversion Low-carbon Utilization, Anhui University of Technology

⁰