Stress corrosion cracking behavior of 16Mn steel and heat-affected zone in alkaline sulfide with different concentrations

HAO Wenkui; LIU Zhiyong; DU Cuiwei; LI Xiaogang

doi:10.3969/j.issn.0438-1157.2013.11.035

您当前的位置：

首页 >

文章列表页 >

Stress corrosion cracking behavior of 16Mn steel and heat-affected zone in alkaline sulfide with different concentrations

更新时间：2025-12-10

- Stress corrosion cracking behavior of 16Mn steel and heat-affected zone in alkaline sulfide with different concentrations
- CIESC Journal Issue 11, Pages: 4143-4152(2013)
- 作者机构：
  
  北京科技大学腐蚀与防护中心,北京,100083
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.11.035
  CLC： G172.4
- Online First：05 November 2013，
  
  Published：05 November 2013
- 稿件说明：
移动端阅览
HAO Wenkui, LIU Zhiyong, DU Cuiwei, et al. Stress corrosion cracking behavior of 16Mn steel and heat-affected zone in alkaline sulfide with different concentrations[J]. CIESC Journal, 2013, (11): 4143-4152.
DOI：

HAO Wenkui, LIU Zhiyong, DU Cuiwei, et al. Stress corrosion cracking behavior of 16Mn steel and heat-affected zone in alkaline sulfide with different concentrations[J]. CIESC Journal, 2013, (11): 4143-4152. DOI： 10.3969/j.issn.0438-1157.2013.11.035.

摘要

利用U形弯试样浸泡实验和电化学技术研究了16Mn钢及其模拟热影响区在不同硫化物浓度的碱性(pH=11.7)介质中的应力腐蚀开裂(SCC)行为与机理。结果表明:16Mn钢原始组织、粗晶组织(空冷组织)和硬化组织(淬火组织)在碱性硫化物环境中均能形成保护性腐蚀产物膜、导致电极过程近似呈钝化状态

钝化电流密度依次降低;淬火组织析氢电流密度较高

腐蚀速度较低

长期服役后会造成靠近熔合线部分腐蚀深度大而暴露出残余拉应力区

引起SCC;HAZ中硬化组织、粗晶组织和原始组织在碱性硫化物环境下SCC敏感性逐渐降低

硬化组织具有较明显的SCC敏感性

粗晶组织和原始组织SCC敏感性小;硫化物浓度升高

16Mn钢及其模拟热影响区SCC敏感性增加;16Mn钢焊缝区在碱性硫化物环境中SCC裂纹扩展机制为阳极溶解机制。

Abstract

This research aims to study the stress corrosion cracking(SCC)behavior and its mechanism of 16Mn steel and heat-affected zone in alkaline(pH=11.7)sulfide solution with different concentrations using electrochemical technology and U-bent specimen immersing test.Original structure

coarse grain structure(air cooling structure)and hardening structure(quenching structure)turned into the state of passivation in alkaline sulfide solution

and the current density of passivation decreased gradually.The current density of hydrogen evolution of hardening organization was higher and corrosion rate was slower.And the corrosion near the fusion line part was deeper and the residual tensile stress area was exposed after long-term service

which caused stress corrosion cracking.The sensitivity of SCC lowered gradually when hardening organization

open grain structure and original structure of HAZ were in alkaline sulfide environment.Hardening structure exhibited high susceptibility to SCC.Coarse grain structure and original structure exhibited low susceptibility to SCC.The susceptibility increased by increasing the concentration of H2S.The SCC mechanism of 16Mn steel was anodic dissolution(AD)and was intergranular fracturing when it was in the solution of alkaline sulfide.

关键词

Keywords

references

Views

743

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Chaos analysis of electrochemical noise and its application in localized corrosion detection

Corrosion health status assessment method for refining unit pipeline based on GLAE-MLP

Study on the protective behavior of heavy-duty anti-corrosive coatings/TA2 in simulated ultra-deep sea 10000 meters environment

Research progress on bio-based anti-corrosion coating

Research on fretting corrosion damage and life prediction of 316L stainless steel based on experiments and finite element analysis

Related Author

XIA Dahai

SONG Shizhe

WANG Jihui

HU Jinqiu

MA Mingjun

ZHANG Laibin

DONG Jiayan

ZHANG Heqi

Related Institution

Tianjin Key Laboratory of Composite and Functional Materials, School of Materials Science and Engineering, Tianjin University

College of Safety and Ocean Engineering, China University of Petroleum

Key Laboratory of Oil and Gas Safety and Emergency Technology, Ministry of Emergency Management

Key Laboratory of Oil and Gas Production Equipment Quality Inspection and Health Diagnosis, State Administration for Market Regulation

College of Chemical Engineering, Zhejiang University of Technology

⁰