Long-term performance of microchannel heat exchanger with folded tube and extruded tube

WEI Wei; XU Kunhao; LIANG Yuanyuan; CHEN Jiangping

doi:10.3969/j.issn.0438-1157.2013.07.009

您当前的位置：

首页 >

文章列表页 >

Long-term performance of microchannel heat exchanger with folded tube and extruded tube

更新时间：2025-12-10

- Long-term performance of microchannel heat exchanger with folded tube and extruded tube
- CIESC Journal Issue 7, Pages: 2369-2375(2013)
- 作者机构：
  
  1. 上海交通大学制冷与低温工程研究所,上海,200240
  2. 萨帕铝热传输(上海)有限公司,上海,201807
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.07.009
  CLC： B65
- Online First：05 July 2013，
  
  Published：05 July 2013
- 稿件说明：
移动端阅览
WEI Wei, XU Kunhao, LIANG Yuanyuan, et al. Long-term performance of microchannel heat exchanger with folded tube and extruded tube[J]. CIESC Journal, 2013, (7): 2369-2375.
DOI：

WEI Wei, XU Kunhao, LIANG Yuanyuan, et al. Long-term performance of microchannel heat exchanger with folded tube and extruded tube[J]. CIESC Journal, 2013, (7): 2369-2375. DOI： 10.3969/j.issn.0438-1157.2013.07.009.

摘要

对采用折叠扁管与传统挤压扁管的微通道换热器长效特性进行了对比研究。分别进行了标准盐雾腐蚀实验

对比腐蚀前后两个换热器样品的换热量、空气侧压降和总热阻变化情况

结果表明

折叠扁管的样品在腐蚀后的各项性能均优于挤压管的样品。传统挤压扁管样件的翅片与扁管连接处率先被腐蚀破坏

14 d腐蚀后就可观察明显的翅片脱落现象

且在28 d腐蚀后挤压扁管上出现泄漏;折叠扁管样件则是翅片率先被腐蚀

而翅片与扁管的连接处没有明显损坏

在49 d腐蚀后折叠扁管没有出现泄漏现象。这是由于折叠扁管能方便地配备保护层

实现牺牲翅片保护扁管的方法

在腐蚀过程中能有效地保护更为重要的扁管。折叠扁管的长效特性优于传统挤压扁管。

Abstract

Corrosion is one of the main characters of Al microchannel heat exchanger.In the present study

standard seawater acidified test (SWAAT)was carried out in microchannel heat exchangers with folded tube and traditional extruded tube

then the performance test and electron metallography analysis were carried on the test samples before and after the corrosion.The result showed that the performance of the sample with folded tube was much better than that with traditional extruded tube after SWAAT.According to the electron metallography analysis

for the test sample with extruded tube

the connection of fins and tubes was damaged first in the SWAAT.Obvious fin debonding occurred after 14 d of SWAAT

and leakage happened on the tube at main body after 28 d of SWAAT.In contrast

the fins of the test sample with folded tube were damaged first in the SWAAT

and no any fin debonding or leakage on the tube occurred after 49 d of SWAAT.The long-term performance of folded tube is better than that of extruded tube.

关键词

Keywords

references

Views

268

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Corrosion health status assessment method for refining unit pipeline based on GLAE-MLP

Study on the protective behavior of heavy-duty anti-corrosive coatings/TA2 in simulated ultra-deep sea 10000 meters environment

Research progress on bio-based anti-corrosion coating

Research on fretting corrosion damage and life prediction of 316L stainless steel based on experiments and finite element analysis

Research progress on mechanism and control strategies of corrosion and plugging in generator stator copper conductors

Related Author

HU Jinqiu

MA Mingjun

ZHANG Laibin

DONG Jiayan

ZHANG Heqi

LU Weizhong

LI Guohua

WANG Hongfei

Related Institution

College of Safety and Ocean Engineering, China University of Petroleum

Key Laboratory of Oil and Gas Safety and Emergency Technology, Ministry of Emergency Management

Key Laboratory of Oil and Gas Production Equipment Quality Inspection and Health Diagnosis, State Administration for Market Regulation

College of Chemical Engineering, Zhejiang University of Technology

State Key Laboratory of Marine Critical Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences

⁰