Modification of end groups of hyperbranched polyester and its film properties

WANG Yong; ZHU Yan'an; QU Jinqing

doi:10.3969/j.issn.0438-1157.2013.06.045

您当前的位置：

首页 >

文章列表页 >

Modification of end groups of hyperbranched polyester and its film properties

更新时间：2025-12-10

- Modification of end groups of hyperbranched polyester and its film properties
- CIESC Journal Issue 6, Pages: 2240-2246(2013)
- 作者机构：
  
  1. 华南理工大学化学与化工学院,广东,广州,510640
  2. 嘉宝莉化工集团股份有限公司,广东,江门,529085
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.06.045
  CLC： 633.14
- Online First：05 June 2013，
  
  Published：05 June 2013
- 稿件说明：
移动端阅览
WANG Yong, ZHU Yan'an, QU Jinqing. Modification of end groups of hyperbranched polyester and its film properties[J]. CIESC Journal, 2013, (6): 2240-2246.
DOI：

WANG Yong, ZHU Yan'an, QU Jinqing. Modification of end groups of hyperbranched polyester and its film properties[J]. CIESC Journal, 2013, (6): 2240-2246. DOI： 10.3969/j.issn.0438-1157.2013.06.045.

摘要

以三羟甲基丙烷为核多元醇

二羟甲基丙酸为AB2型单体

对甲苯磺酸为催化剂准一步法合成了第二代超支化聚酯(HBP-0)。HBP-0分别经己内酯和月桂酸改性得到改性超支化聚酯(HBPs)。采用FT-IR、1H NMR和GPC对HBP-0的结构和相对分子质量进行表征

发现超支化聚酯的支化度为0.43

相对分子量与理论相对分子量比较接近

相对分子质量分布系数只有1.72。以甲苯二异氰酸酯加成物为交联剂

考察了改性超支化聚酯交联涂膜性能

结果表明

3种改性超支化聚酯的涂膜性能在光泽度、耐冲击性、附着力和柔韧性方面表现十分优异。其中HBP-3同时用己内酯和月桂酸改性具有最佳性能

黏度最低为7500 mPa·s

涂膜表干40 min

且硬度达到F。而单独用己内酯或月桂酸改性的HBP-1和HBP-2的相应数据分别为7×105 mPa·s、20 min和HB及17500 mPa·s、90 min和2B。

Abstract

The second generation hyperbranched polyester (HBP-0) was synthesized by the pseudo-one step method with 2

2-bis (hydroxyl-methyl) propionic acid as AB2 monomer

trimethylolpropane as core monomer and p-toluene sulfonic acid as catalyst.HBP-0 was modified with ε-caprolactone and lauric acid to prepare modified hyperbranched polyesters (HBP-1

HBP-2

and HBP-3).The structure and molecular weight of HBPs were characterized by FT-IR

1H NMR and GPC.HBP-0 was synthesized with 0.43 degree of branching and its molecular weight approached the theoretical value and distribution factor was 1.72.The film properties of modified HBPs cured by toluene diisocyanate adduct were studied

and the results showed that the modified HBPs displayed excellent film properties in the gross

impact resistance

adhesion and flexibility.HBP-3 modified by both ε-caprolactone and lauric acid exhibited the best properties

including lowest viscosity up to 7500 mPa·s

surface drying time of 40 min and pencil hardness of F.While the corresponding data of HBP-1 and HBP-2 modified only by ε-caprolactone or lauric acid were 7×105 mPa·s

20 min and HB; 17500 mPa·s

90 min and 2B

respectively.

关键词

Keywords

references

Views

762

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress of water-soluble polymer viscosity reducer

Experimental study of solubility and viscosity of R513A and PVE lubricants

Effect of NdF3 content on local structure and transport properties of NdF3-LiF molten salt

Hypergolic ignition characteristics and propulsion performance of imidazolium dicyanamide ionic liquids blended with furfuryl alcohol

Experimental study on viscosity of high purity air at low temperatures

Related Author

ZHANG Fumin

WANG Yefei

WANG Hongbo

DING Mingchen

CHEN Wuhua

LIAO Jian

LIU Jianbin

HUANG Zhixue

Related Institution

State Key Laboratory of Deep Oil and Gas, China University of Petroleum (East China)

Shandong Key Laboratory of Oil and Gas Field Chemistry, China University of Petroleum (East China)

Research Institute of Exploration and Development，PetroChina Xinjiang Oilfield Company

College of Petroleum Engineering, Xi’an Shiyou University

School of Mechanical Engineering, Tianjin University

⁰