Preparation of melamine-modified lignin and its adsorption performance for silver ion

WANG Wendong; ZHANG Jianwei; ZHENG Jifeng; LV Qiufeng

doi:10.3969/j.issn.0438-1157.2013.04.049

您当前的位置：

首页 >

文章列表页 >

Preparation of melamine-modified lignin and its adsorption performance for silver ion

更新时间：2025-12-10

- Preparation of melamine-modified lignin and its adsorption performance for silver ion
- CIESC Journal Issue 4, Pages: 1478-1484(2013)
- 作者机构：
  
  福州大学材料科学与工程学院,福建,福州,350116
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.04.049
  CLC： Q317TQ319
- Online First：05 April 2013，
  
  Published：05 April 2013
- 稿件说明：
移动端阅览
WANG Wendong, ZHANG Jianwei, ZHENG Jifeng, et al. Preparation of melamine-modified lignin and its adsorption performance for silver ion[J]. CIESC Journal, 2013, (4): 1478-1484.
DOI：

WANG Wendong, ZHANG Jianwei, ZHENG Jifeng, et al. Preparation of melamine-modified lignin and its adsorption performance for silver ion[J]. CIESC Journal, 2013, (4): 1478-1484. DOI： 10.3969/j.issn.0438-1157.2013.04.049.

摘要

以酶解木质素、三聚氰胺和甲醛为原料

通过接枝反应制备三聚氰胺改性酶解木质素(MEHL)

并研究MEHL对银离子的吸附性能。接枝反应的研究结果表明

三聚氰胺和甲醛的添加量对产率有很大影响。酶解木质素、三聚氰胺、甲醛质量比为10:6:6

于90℃下反应4 h

所制得的MEHL的产率可达83.7%。红外光谱、热重和元素分析的结果表明

三聚氰胺成功接枝到酶解木质素分子上。MEHL的含氮量由酶解木质素的0.81%提高到18.55%。银离子的吸附研究表明

MEHL对银离子表现出很好的吸附性能。在银离子初始浓度为0.16 mol·L-1

在MEHL用量为50 mg

吸附温度为30℃时吸附36 h

MEHL对银离子的吸附容量为944.1 mg·g-1。

Abstract

Melamine-modified lignin (MEHL) was prepared using grafting reaction from hydrolyzed lignin (EHL) by enzyme

melamine and formaldehyde

and its adsorption for silver ions was studied.The results from grafting reaction showed that content of melamine and formaldehyde had great influences on MEHL yield.High yield 83.7% for MEHL was achieved with EHL:melamine:formaldehyde mass ratio 10:6:6 at reaction temperature 90℃ and reaction time 4 h.The MEHL obtained was characterized by FTIR

TGA and elemental analysis.The results showed that melamine molecules had been grafted onto EHL chains.Nitrogen content in MEHL had obvious increase from original 0.81% to 18.55%.Furthermore

the adsorption performance for silver ions at the same conditions was much stronger for MEHL than for EHL.Its maximum adsorption capacity was up to 944.1 mg·g-1 at optimal conditions:50 mg MEHL

initial silver ion concentration 0.16 mol·L-1

30℃ and 36 h.

关键词

Keywords

references

Views

392

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Hydroxypropyl sulfomethylation modification of lignin and its effect on cellulase hydrolysis

One-step preparation of oxygen-enriched lignin activated carbon and its methylene blue adsorption performance

Chemical modification of lignin and its adsorption to AuCl4-

Influence of carboxymethylated lignin as pesticide dispersant on adsorptionand dispersion

Adsorption of cadmium and lead ions onto regenerated lignin from pretreatment liquid of rapeseed stalk

Related Author

HUANG Lijing

HUANG Jijiao

LI Penghui

LIU Zhinuo

JIANG Kangjie

WU Wenjuan

WANG Jing

HAN Qiaoning

Related Institution

Innovation Center of Efficient Processing and Utilization of Forest Resources, Nanjing Forestry University

School of Chemistry and Chemical Engineering, Guangxi University for Nationalities

Guangxi Key Laboratory of Chemistry and Engineering of Forest Products, Guangxi Collaborative Innovation Center of Forest Chemistry and Engineering

State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology

Key Laboratory for Ferrous Metallurgy and Resources Utilization, Ministry of Education, Wuhan University of Science and Technology

⁰