Preparation of PDMS/SiO<sub>2</sub> nanocomposites via miniemulsion polymerization

YANG Lei; XU Yongshen; QIU Shouji; ZHANG Ya

doi:10.3969/j.issn.0438-1157.2013.04.048

您当前的位置：

首页 >

文章列表页 >

Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization

更新时间：2025-12-10

- Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization
- CIESC Journal Issue 4, Pages: 1473-1477(2013)
- 作者机构：
  
  天津大学化工学院,天津,300072
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.04.048
  CLC： 635
- Online First：05 April 2013，
  
  Published：05 April 2013
- 稿件说明：
移动端阅览
YANG Lei, XU Yongshen, QIU Shouji, et al. Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization[J]. CIESC Journal, 2013, (4): 1473-1477. DOI: 10.3969/j.issn.0438-1157.2013.04.048.
DOI：

YANG Lei, XU Yongshen, QIU Shouji, et al. Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization[J]. CIESC Journal, 2013, (4): 1473-1477. DOI: 10.3969/j.issn.0438-1157.2013.04.048. DOI：

摘要

采用超声分散的方法

以少量八甲基环四硅氧烷(D4)对硅溶胶粒子进行表面接枝改性。然后在改性硅溶胶存在下

以十二烷基苯磺酸(DBSA)为乳化剂兼催化剂进行D4的微滴乳液聚合

得到聚硅氧烷(PDMS)/二氧化硅(SiO2)纳米复合乳液。采用FTIR、TGA、纳米粒度仪、TEM和拉力机分别对样品进行了表征。结果表明:采用超声分散的方法

能够有效地实现硅溶胶粒子的表面改性。通过微滴乳液聚合得到的复合乳胶粒是聚合物包覆二氧化硅粒子的核壳结构形态。SiO2的引入提高了有机硅复合膜力学性能

增强了热稳定性。

Abstract

Ultrasonic dispersion process was utilized to modify silica sol nanoparticles with a small amount of D4.Then in the presence of modified silica sol

miniemulsion polymerization of D4 was conducted with DBSA as emulsifier and catalyst

and polydimethylsiloxane(PDMS)/SiO2 nanocomposites emulsion latex was obtained.Modified silica sol particles were characterized by FTIR and TGA.The diameter and morphology of the composite latex particles were analyzed by nano particle size analyzer and TEM

respectively.Mechanical properties and thermal stability of the composite films were characterized by tensile test and TGA.The results showed that ultrasonic dispersion was an effective way to modify silica sol particles.Modified silica sol particles could be encapsulated by polydimethylsiloxane and form core-shell latex particle morphology during miniemulsion polymerization.Introduction of SiO2 improved mechanical properties and thermal stabilities of polysiloxane composite films.

关键词

Keywords

references

Views

420

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Nanocomposites prepared insitu miniemulsion polymerization with silica sol

Synthesis and thermal stability of α, ω-hydroxy-terminated phenyl/phenylene-containing polysiloxanes with high vinyl content

Preparation and mass transfer efficiency of three-dimensional network extraction membrane

Effect of graphene/polyaniline modified anode on performance of microbial fuel cell

Facile synthesis of MWCNT/SiO2 nano-composites as high-performance oil adsorbents

Related Author

黄志娟

ZHANG Junying

SHI Ling

WANG Chengzhong

ZHANG Xiao'a

SHEN Peixin

LI Ziyang

CHEN Huayan

Related Institution

School 

Key Laboratory of Carbon Fiber and Functional Polymers of Ministry of Education, College of Materials Science and Engineering, Beijing University of Chemical Technology

State Key Laboratory of Separation Membrane and Membrane Process, Tiangong University

School of Materials Science and Engineering, Tiangong University

School of Environmental Science and Engineering, Tiangong University

⁰

Preparation of PDMS/SiO2 nanocomposites via miniemulsion polymerization

DOI：10.3969/j.issn.0438-1157.2013.04.048

摘要

Abstract

关键词

Keywords

references

Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization