High infrared reflective chromic oxide green pigment prepared by thermal decomposition of CrO₃ doped with V₂O₅

更新时间：2025-12-10

- High infrared reflective chromic oxide green pigment prepared by thermal decomposition of CrO₃ doped with V₂O₅
- CIESC Journal Issue 10, Pages: 3316-3323(2012)
- 作者机构：
  
  1. 中国科学院过程工程研究所,北京,100190
  2. 湿法冶金清洁生产技术国家工程实验室,北京,100190
  3. 中国科学院研究生院,北京,100190
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.10.044
  CLC： Q136.1
- Online First：05 October 2012，
  
  Published：05 October 2012
- 稿件说明：
移动端阅览
ZHOU Zhen, LI Ping, ZHANG Hongling, et al. High infrared reflective chromic oxide green pigment prepared by thermal decomposition of CrO₃ doped with V₂O₅[J]. CIESC Journal, 2012, (10): 3316-3323. DOI: 10.3969/j.issn.0438-1157.2012.10.044.
DOI：

ZHOU Zhen, LI Ping, ZHANG Hongling, et al. High infrared reflective chromic oxide green pigment prepared by thermal decomposition of CrO₃ doped with V₂O₅[J]. CIESC Journal, 2012, (10): 3316-3323. DOI: 10.3969/j.issn.0438-1157.2012.10.044. DOI：

摘要

研究了铬酸酐热分解制备高性能红外反射氧化铬绿颜料

在优化现有铬酸酐热分解工艺的基础上

详细探讨了掺杂制备红外反射氧化铬绿颜料的工艺条件和相关机理。借助UV-vis-NIR、FT-IR、SEM、XRD和CIE-L*a*b*等手段发现:在铬酸酐热分解过程中

不同的热分解温度导致粒径变化

从而影响红外反射率;优化的制备工艺条件(热分解温度1250℃、热分解时间0.5 h)下

氧化铬绿的红外反射率达到90%。在掺杂过程中

V2O5的添加可使氧化铬绿的最高红外反射率达到98%。随着V2O5添加量的增加

红外反射率先增加后减少;当V/Cr摩尔比为0.004时

红外反射率、电导率、介电常数都达到极值

三者呈现一致的规律性变化。初步机理探索表明

氧化铬本征导电类型为空穴导电

掺杂V2O5以后导电类型发生改变

伴随着电阻率的变化

氧化铬吸收和反射光子能力改变

从而影响红外反射性能。

Abstract

A CrO3 thermal decomposition process was used to prepare high infrared reflective chromic oxide green pigment.On the basis of optimized conditions of thermal decomposition of CrO3

the doping conditions and the related mechanism to prepare high infrared reflective chromic oxide green pigment were investigated.Through UV-vis-NIR

FT-IR

SEM

XRD and CIE-L*a*b* analysis

key factors such as thermal decomposition temperature and dopant were studied.In the thermal decomposition step

particle size

as well as infrared reflectance of the chromic oxide green pigment was dependent on decomposition temperature.Under the optimized conditions of 1250℃ and 0.5 h

the infrared reflectivity of the obtained products could be as high as 90%.In the doping step

the maximum reflectivity of the chromic oxide green pigment could reach 98% with doping V2O5.As the content of the V2O5 dopant increased

the infrared reflectivity of the chromic oxide green pigment firstly increased and then decreased;conductivity and dielectric constant followed the same tendency.The mechanism showed that conductive type of the chromic oxide green pigment transformed with V2O5 addition

and change in conductivity resulted in subsequent change in absorptive and reflective capability of photon. At last

the infrared reflectance of the chromic oxide green pigment was improved.

关键词

Keywords

references

Views

248

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Utilizing organic acids for V2O5 recovery from denitration catalyst alkaline inactivation

Effect of Fe2O3 on surface properties and activities of V2O5-WO3/TiO2 catalysts

Performance of V2O5-WO3-MoO3/TiO2 catalyst for diesel engine NH3-SCR system

Influence of alkali metal compound on low-temperature NH3-SCR of NO over V2O5/AC catalyst

Properties of sulfation supported V/Ti denitration catalyst

Related Author

CHEN Fengqiao

CUI Chang

QI Liqiang

LIU Jianhua

YANG Xiaobo

ZHANG Chen

WU Fan

LI Zhong

Related Institution

Department of Environment Science and Engineering, North China Electric Power University

School of Chemistry and Chemical Engineering, South China University of Technology

Kenchuang Environmental Technology Company of Jiangsu

School of Energy and Power Engineering, Shandong University

School of Mechanical Engineering, The University of Birmingham, Birmingham B12.2TT

⁰