Effect of Ca-compound on low temperature synthesis of AlN ultrafine powders by Carbothermal Reduction Nitride route from a sol-gel precursor

杨清华

doi:10.3969/j.issn.0438-1157.2012.06.037

您当前的位置：

首页 >

文章列表页 >

Effect of Ca-compound on low temperature synthesis of AlN ultrafine powders by Carbothermal Reduction Nitride route from a sol-gel precursor

更新时间：2025-12-10

- Effect of Ca-compound on low temperature synthesis of AlN ultrafine powders by Carbothermal Reduction Nitride route from a sol-gel precursor
- CIESC Journal Issue 6, Pages: 1907-1912(2012)
- 作者机构：
  
  中国计量学院材料科学与工程学院,浙江,杭州
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.06.037
  CLC： 611.4TB321
- Online First：05 June 2012，
  
  Published：05 June 2012
- 稿件说明：
移动端阅览
杨清华. Effect of Ca-compound on low temperature synthesis of AlN ultrafine powders by Carbothermal Reduction Nitride route from a sol-gel precursor[J]. CIESC Journal, 2012, (6): 1907-1912.
DOI：

杨清华. Effect of Ca-compound on low temperature synthesis of AlN ultrafine powders by Carbothermal Reduction Nitride route from a sol-gel precursor[J]. CIESC Journal, 2012, (6): 1907-1912. DOI： 10.3969/j.issn.0438-1157.2012.06.037.

摘要

以硝酸铝、葡萄糖和硝酸钙为原料，通过溶胶-凝胶工艺获得了组分均匀的Al2O3、C和CaO前驱体，进而利用碳热还原反应合成超细氮化铝粉体，探讨了钙助剂对氮化铝合成温度及粉体颗粒生长的影响规律。结果表明：钙助剂的添加，通过与前驱体中氧化铝在较低温度下发生反应，先后生成CaAl4O7、Ca3Al10O18、CaAl2O4和Ca12Al14O33等铝酸钙相；上述铝酸钙相能在较低温度下形成液相，可有效促进氮化铝的合成和粉体颗粒的生长，从而在1400 ℃合成纯相氮化铝。当原料中钙铝摩尔比为0.0262时，在1350 ℃氮化得到了粒径60-80 nm的氮化铝粉体，仅有少量铝酸钙相存在；当氮化温度上升至1400 ℃时，铝酸钙相因挥发而消失，得到粒径100-180 nm的单相氮化铝粉体。

Abstract

AlN ultrafine powders were synthesized at low temperature by Carbothermal Reduction Nitride (CRN) route from a sol-gel precursor by using aluminum nitrate

glucose and calcium nitrate as raw materials. The influence of Ca-compound on the phase transformation behavior of the precursors

as well as the particle size and morphology of synthesized AlN powders

were investigated. X-ray diffraction patterns showed that Ca-compound reacted with alumina powder and resulted in aluminate phase of CaAl4O7

Ca3Al10O18

CaAl2O4 and Ca12Al14O33. Those aluminate phases formed liquid during the nitradation process

which promoted the transformation of Al2O3 to AlN and vaporized at high temperature. Compared to the approach without additive

the use of Ca-compound addition reduced the synthesis temperature of AlN from 1500 ℃ to 1400 ℃. SEM photographs showed that AlN powders synthesized with Ca-compound addition were larger than those without Ca addition

and high doping of Ca-compound lead to the growth of AlN powders. With [Ca]/[Al] of 0.0262

the particle sizes of AlN powders synthesized at 1350 ℃ were 60-80 nm. When the nitradation temperature was increased to 1400 ℃

the single AlN with the particle sizes of 100-180 nm was obtained.

关键词

Keywords

references

Views

383

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on stress evolution and hopper design of ultrafine powder under aeration conditions

Controlled synthesis of Bi2MoO6/MoO3 composite fibers via in-situ hydrothermal method and their high-efficiency photocatalytic hydrogen production performance

Thermodynamic performance of tower-type solar-assisted supercritical compression CO2 energy storage system

New universal corresponding state equation for correlation and extrapolation of saturated vapor-liquid density

Identification of gas-liquid two-phase flow patterns in a riser based on recursive characteristics and CNN

Related Author

CHEN Luming

LIU Yingli

LU Haifeng

GAN Qiaoyu

CHANG Ying

CHEN Lu'ming

LIU Ying'li

LU Hai'feng

Related Institution

State Key Laboratory of NBC Protection for Civilian

State Key Laboratory of Coal Liquification, Gasification and Utilization with High Efficiency and Low Carbon Technology, Institute of Clean Coal Technology, East China University of Science and Technology

State Key Laboratory of Coal Liquification, Gasification and Utilization with High Efficiency and Low Carbon Technology, East China University of Science and Technology, Institute of Clean Coal Technology

⁰