Electrochemical behavior of Li incorporation into Al in LiTFSI/NaTf organic molten salt

更新时间：2025-12-10

- Electrochemical behavior of Li incorporation into Al in LiTFSI/NaTf organic molten salt
- CIESC Journal Issue 5, Pages: 1498-1503(2012)
- 作者机构：
  
  1. 1嘉兴学院生物与化学工程学院
  2. 浙江工业大学应用化学系，绿色化学合成技术国家重点实验室培育基地
  3. 嘉兴市化工清洁工艺重点实验室
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.05.025
  CLC： 646
- Online First：05 May 2012，
  
  Published：05 May 2012
- 稿件说明：
移动端阅览
屠晓华. Electrochemical behavior of Li incorporation into Al in LiTFSI/NaTf organic molten salt[J]. CIESC Journal, 2012, (5): 1498-1503.
DOI：

屠晓华. Electrochemical behavior of Li incorporation into Al in LiTFSI/NaTf organic molten salt[J]. CIESC Journal, 2012, (5): 1498-1503. DOI： 10.3969/j.issn.0438-1157.2012.05.025.

摘要

采用循环伏安、计时电流和恒电流充放电等电化学测试技术考察了LiTFSI/NaTf熔盐电解质中锂在铝电极上的电化学行为。研究结果表明：在该熔盐中，锂在铝电极上的电化学还原过程伴随着锂铝合金的成核过程，且反应生成的LiAl合金只有一种合金相是可逆的；恒电流循环充放电实验发现，首次循环的库仑效率较低，库仑效率随电流密度的增大而有所减小，但随温度的升高而增大。计时电流实验发现，锂原子嵌入铝电极中形成α-LiAl合金的过程受锂在铝基体内扩散步骤控制，且该扩散系数为1.7×10-10 cm2·s-1。

Abstract

The electrochemical behavior of lithium incorporation into aluminum electrode in LiTFSI/NaTf molten salt electrolyte was studied with electrochemical techniques，including cyclic voltammetry，chronopotentiometry and chronoamperometry.The reduction reaction was found to involve a nucleation process at the aluminum electrode，and only one LiAl alloy phase was reversible.The galvanostatic cycle experiments showed that the coulombic efficiency was very low in the first cycle and decreased with increasing current density，and increased with increasing operating temperature.The results of chronoamperometry indicated that the incorporation of lithium into aluminum for the formation of α-phase Li-Al alloy was limited by its rate of diffusion，with a measured diffusion coefficient of 1.7×10-10 cm2·s-1.

关键词

Keywords

references

Views

398

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress of high temperature proton exchange membranes

Influence of magnetic field on jet impingement heat transfer with molten salt

Startup and isothermal performance of high-temperature molten salt heat pipe

Numerical study of transient heat transfer performance for molten salt receiver tube

Heat transfer characteristic of molten salt in transverse corrugated tube with semi-circumference heating

Related Author

XU Tongwen

YANG Zhengjin

LI Hui

MA Chongfang

GAO Feng

CHEN Yongchang

ZHAO Jinlong

WANG Gang

Related Institution

School of Chemistry and Material Science, University of Science and Technology of China

College of Environmental and Energy Engineering, Beijing University of Technology, Key Laboratory of Enhanced Heat Transfer and Energy Conservation, Ministry of Education, Key Laboratory of Heat Transfer and Energy Conversion, Beijing Education Commission

Beijing Key Laboratory of Heating, Gas Supply, Ventilating and Air Conditioning Engineering, Beijing University of Civil Engineering and Architecture

Key Laboratory of Enhanced Heat Transfer and Energy Conservation of Ministry of Education, Beijing University of Technology

Henan Dongda High Temperature Energy-Saving Material Co., Ltd.

⁰