Preparation of Fe<sub>3</sub>O<sub>4</sub>/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template

张宝亮

doi:10.3969/j.issn.0438-1157.2012.04.043

您当前的位置：

首页 >

文章列表页 >

Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template

更新时间：2025-12-10

- Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template
- CIESC Journal Issue 4, Pages: 1308-1314(2012)
- 作者机构：
  
  西北工业大学理学院应用化学系,陕西,西安
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.04.043
  CLC： Q31O611.62
- Online First：05 April 2012，
  
  Published：05 April 2012
- 稿件说明：
移动端阅览
张宝亮. Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template[J]. CIESC Journal, 2012, (4): 1308-1314. DOI: 10.3969/j.issn.0438-1157.2012.04.043.
DOI：

张宝亮. Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template[J]. CIESC Journal, 2012, (4): 1308-1314. DOI: 10.3969/j.issn.0438-1157.2012.04.043. DOI：

摘要

介绍了一种以大孔高比表面积甲基丙烯酸缩水甘油酯（GMA）与二甲基丙烯酸乙二醇酯（EGDMA）共聚交联微球［P(GMA-co-EGDMA)］为模板制备磁性复合微球的简单方法。制备过程包括Fe3+和Fe2+的浸入、OH-作用下孔内铁离子的共沉淀两步。在此过程中考察了浸泡温度、浸泡时间、共沉淀温度以及沉积次数对微球磁含量的影响，确定最佳制备工艺为50℃浸泡4 h，70℃反应1 h，如此反复4次磁含量可以达到45.24%。并通过SEM、VSM、XRD、TGA及压汞仪、激光粒度仪等手段对Fe3O4/P(GMA-co-EGDMA)的形貌、比饱和磁化强度、磁含量及孔性能进行了表征，微球的粒径范围处于100～200 μm之间，平均粒径为162 μm，比饱和磁化强度为10.92 emu·g-1，平均孔径及比表面积分别为60 nm和116 m2·g-1。

Abstract

A simple method for preparation of Fe3O4/P(GMA-co-EGDMA)magnetic composite microspheres using microporous P(GMA-co-EGDMA)microspheres copolymerized with glycidyl methacrylate（GMA)and ethylene glycol dimethacrylate（EGDMA)as template is reported in this paper. The preparation process included soaking of ferrous ion and ferric ion and coprecipitation in the presence of OH-.The influences of soaking temperature

soaking time

coprecipitation temperature and deposition times on magnetic content of magnetic composite microspheres were studied.The optimum preparation process of microporous Fe3O4/P(GMA-co-EGDMA)magnetic composite microspheres was as follows：microporous P(GMA-co-EGDMA)microspheres were soaked at 50℃for 4 h

coprecipitation temperature and time were 70℃ and 1 h respectively.The magnetic content of magnetic composite microspheres was 45.24% when the deposition process was repeated 4 times.The morphology

magnetic properties

magnetic content

pore performance and particle size distribution of Fe3O4/P(GMA-co-EGDMA)were determined by SEM

TGA

XRD

mercury porosimeter and laser particle sizer.It was found that the range of particle size of Fe3O4/P(GMA-co-EGDMA)was 100～200 μm and average particle size was 162 μm

specific saturation magnetization was 10.92 emu·g-1

average pore diameter and specific surface area were 60 nm and 116 m2·g-1 respectively.

关键词

Keywords

references

Views

1040

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

O2 generation path in Fe2+/H2O2 system

Influences of Fe2+/Fe3+ and Mn2+ on total nitrogen removal and nitrogen transformations during low-oxygen aeration

Effect of ceramic matrices on dispersion of loaded catalyst and DeNOx activity of catalytic filters

Influence mechanism of H2S on reactivity of NiFe2O4 oxygen carriers for chemical looping combustion

Indirect sulfation characteristics of limestone under O2/H2O combustion atmosphere

Related Author

ZHAO Haiqian

GAO Xingcun

WANG Zhonghua

GAO Jihui

Bin CUI

Runyu LIU

Zhibin LIU

Qing YANG

Related Institution

Institute of Civil Engineering & Architecture, Northeast Petroleum University

College of Energy Science and Engineering, Harbin Institute of Technology

College of Environmental and Energy Engineering, Beijing University of Technology

School of Chemical Engineering, Xiangtan University

State Key Laboratory of Multi-phase Complex Systems, Institute of Process Engineering, Chinese Academy of Sciences

⁰

Preparation of Fe3O4/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template

DOI：10.3969/j.issn.0438-1157.2012.04.043

摘要

Abstract

关键词

Keywords

references

Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template