Preparation and properties of novel UV-curable waterborne epoxy and acrylate modified polyurethane

更新时间：2025-12-10

- Preparation and properties of novel UV-curable waterborne epoxy and acrylate modified polyurethane
- CIESC Journal Issue 4, Pages: 1264-1273(2012)
- 作者机构：
  
  华南理工大学化学与化工学院,广东,广州
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.04.038
  CLC： Q050.425
- Online First：05 April 2012，
  
  Published：05 April 2012
- 稿件说明：
移动端阅览
魏丹. Preparation and properties of novel UV-curable waterborne epoxy and acrylate modified polyurethane[J]. CIESC Journal, 2012, (4): 1264-1273.
DOI：

魏丹. Preparation and properties of novel UV-curable waterborne epoxy and acrylate modified polyurethane[J]. CIESC Journal, 2012, (4): 1264-1273. DOI： 10.3969/j.issn.0438-1157.2012.04.038.

摘要

合成了一种新型的具有高交联密度和优异涂膜性能的环氧树脂和丙烯酸酯同时改性的紫外线（UV）固化水性聚氨酯（UV-EP-AC-WPUD）。通过环氧基团与以异氰酸酯基团（-N=C=O）封端的聚氨酯预聚体之间的反应引入质量分数为4%的环氧树脂E-20。同时，通过聚氨酯链的-N=C=O与二元丙烯酸酯（PEDA）以及季戊四醇三丙烯酸酯（PETA）的羟基之间的反应引入碳碳双键（C=C），C=C的含量达到4.65 meq·g-1。质量分数为3%的光引发剂Irgacure 2959被用于引发涂膜中C=C的聚合，涂膜的凝胶含量在12 s UV辐射之后达到91%，意味着C=C的聚合和交联速度快，同时所得到的涂膜的交联度非常高，不溶于溶剂丙酮，测试表明环氧树脂和两种丙烯酸酯单体已经成功嵌入聚氨酯链中，涂膜具有优异的力学性能和化学性能。

Abstract

In order to improve the mechanical and chemical properties

especially the solvent resistance of the cast films formed from normal waterborne polyurethane (PU) dispersions

a novel ultraviolet (UV)-curable epoxy and acrylate-modified waterborne polyurethane dispersion (UV-EP-AC-WPUD) and its film with high crosslinking density and excellent film properties were prepared and studied.4% epoxy resin E-20 was introduced in PU chain by grafting reaction between epoxy resin and polyurethane prepolymer terminated with the –N=C=O group.The C=C bond was introduced in PU chain by the chain-extending reaction of —NCO in polyurethane prepolymer with two hydroxyl vinyl monomers PEDA and single-hydroxyl vinyl monomers PETA

and the obtained maximum C=C content was up to 4.65 meq·g-1. 3% photoinitiator Irgacure 2959 was used to initiate the polymerization of C=C bond in cast films

and the gel content of the UV-EP-AC-WPUD films could reach up to 91% after 12 s UV-radiation

which meant the polymerization rate and crosslinking rate of C=C bond was high

and the obtained UV-EP-AC-WPUD film was highly-crosslinked and insoluble in solvent.The water absorption

solvent resistance

gel content

pendulum hardness and tensile strength of the cured film were studied

and Fourier transform infrared spectroscopy (FTIR) analysis and film study results showed that the UV-cured EP-AC-WPUD films including epoxy resins and hydroxyl-containing vinyl monomers had excellent mechanical and chemical properties. Thermo gravimetric analysis (TGA) also indicated that the thermal stability of the film was improved significantly.

关键词

Keywords

references

Views

564

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Synthesis and photoinitiation property of a cinnamyl formamide disulfide compound

Conditions and process of pervaporation benzene/cyclohexane mixture by waterborne polyurethane membranes

Preparation and property of waterborne polyurethane-based ITO etching ink

Preparation and characterization of carboxylate/sulfonate composite WPU emulsion adhesive

Crystallization kinetics parameters of waterborne polyurethane and its application in adhesive for shoes

Related Author

CUI Ruixue

ZHANG Yuhan

SUN Fang

YAO Lulu

YE Hui

SONG Ying

CUI Peng

HUANG Jiajian

Related Institution

College of Chemistry, Beijing University of Chemical Technology

Anqing Research Institute, Beijing University of Chemical Technology

School of Chemistry and Chemical Engineering, Hefei University of Technology

College of Materials and Energy, South China Agricultural University

College of Chemistry and Environmental Engineering, Dongguan University of Technology

⁰