Synthesis of PS-b-P4VP and microphase separation morphology of its thin film

LI Zhifang; XU Zhiguang; JIANG Shan; YU Qiang

doi:10.3969/j.issn.0438-1157.2012.04.023

您当前的位置：

首页 >

文章列表页 >

Synthesis of PS-b-P4VP and microphase separation morphology of its thin film

更新时间：2025-12-10

- Synthesis of PS-b-P4VP and microphase separation morphology of its thin film
- CIESC Journal Issue 4, Pages: 1149-1155(2012)
- 作者机构：
  
  常州大学材料科学与工程学院
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.04.023
  CLC： 631.1
- Online First：05 April 2012，
  
  Published：05 April 2012
- 稿件说明：
移动端阅览
LI Zhifang, XU Zhiguang, JIANG Shan, et al. Synthesis of PS-b-P4VP and microphase separation morphology of its thin film[J]. CIESC Journal, 2012, (4): 1149-1155.
DOI：

LI Zhifang, XU Zhiguang, JIANG Shan, et al. Synthesis of PS-b-P4VP and microphase separation morphology of its thin film[J]. CIESC Journal, 2012, (4): 1149-1155. DOI： 10.3969/j.issn.0438-1157.2012.04.023.

摘要

通过原子转移自由基聚合（ATRP）方法制备了聚苯乙烯-b-聚（4-乙烯基吡啶）二嵌段共聚物（PS-b-P4VP），使用核磁共振（1H NMR）和凝胶渗透色谱（GPC）对嵌段共聚物进行了表征。将PS-b-P4VP/三氯甲烷溶液旋涂成膜，使用原子力显微镜（AFM）观察热处理条件对薄膜微相分离形貌的影响。结果表明，PS-b-P4VP薄膜会发生微相分离，形成以PS链段为分散相、P4VP链段为连续相基体的纳米尺度微相分离形貌。热处理条件的改变使薄膜呈现不同程度的微相分离形貌结构，提高热处理温度以及延长热处理时间均有利于促进嵌段共聚物的微相分离，使微相分离程度加大。在150℃、24 h的热处理条件下，PS-b-P4VP薄膜形成了PS微相区以规则的柱状形态在薄膜表面突起的微相分离形貌，且分布均匀，界面清晰。

Abstract

Self-assembly in thin films of block copolymer of polystyrene and poly(4-vinylpyridine) （PS-b-P4VP）derived by the immiscibility between the constituted blocks could create rich morphologies with nanometer scale periodic patterns over large areas

leading to potential applications in nanotemplates

nanopatterns

and selective separation membrance with well-defined channel size.The microphase separation behavior and the resulting morphological structure have attracted more attention from investigators.In this paper

diblock copolymer of PS-b-P4VP was synthesized using atom transfer radical polymerization(ATRP) and its structure was characterized by 1H NMR and GPC.The block copolymer was dissolved in chloroform and PS-b-P4VP thin film was prepared by spin coating.Atomic force microscope(AFM) was used to observe the microphase separation morphologies of PS-b-P4VP thin films obtained under different conditions of heat treatment.It was found that microphase separation occurred in PS-b-P4VP film

generating nanoscale microphase separation morphology with PS microphase as dispersion phase and P4VP as continuous phase matrix.The film exhibited different microphase separation morphologies under different heat treatment conditions.Increasing temperature and/or prolonging time in the heat treatment process of PS-b-P4VP film accelerated the microphase separation in the film.After being treated at 150℃ for 24 h

PS-b-P4VP film demonstrated a microphase separation morphology with column-shaped PS microphases projecting from the P4VP matrix.The column-shaped PS microphases were uniformly distributed on the surface of the film and the interface was clear.

关键词

Keywords

references

Views

958

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of ultrathin Cu3(BTC)2 film by heat treatment of layer-by-layer deposition

Micro-phase separation morphologies in thin films of PS-b-P4VP tuned by blending with homopolymers

Effect of heat treatment on structural character and desulfurization capability of palygorskite

Corrosion health status assessment method for refining unit pipeline based on GLAE-MLP

Study on entropy wave production and dissipation in partially premixed swirl flames subject to inlet perturbations

Related Author

QIU Longyun

LI Licheng

FENG Xin

FU Shuangqin

ZHANG Suoying

LU Xiaohua

YANG Zhuhong

ZHU Mengbing

Related Institution

State Key Laboratory of Materials-Oriented Chemical Engineering, School of Chemistry and Chemical Engineering, Nanjing University of Technology

Jiangsu Key Laboratory for Solar Cell Materials and Technology, School of Materials Science and Engineering, Changzhou University

合肥工业大学化学工程学院

⁰