Recovery of titanium from titanium-bearing blast furnace slag by ammonium sulfate melting method

王思佳

doi:10.3969/j.issn.0438-1157.2012.03.045

您当前的位置：

首页 >

文章列表页 >

Recovery of titanium from titanium-bearing blast furnace slag by ammonium sulfate melting method

更新时间：2025-12-10

- Recovery of titanium from titanium-bearing blast furnace slag by ammonium sulfate melting method
- CIESC Journal Issue 3, Pages: 991-995(2012)
- 作者机构：
  
  东北大学材料与冶金学院
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.03.045
  CLC：
- Online First：05 March 2012，
  
  Published：05 March 2012
- 稿件说明：
移动端阅览
王思佳. Recovery of titanium from titanium-bearing blast furnace slag by ammonium sulfate melting method[J]. CIESC Journal, 2012, (3): 991-995.
DOI：

王思佳. Recovery of titanium from titanium-bearing blast furnace slag by ammonium sulfate melting method[J]. CIESC Journal, 2012, (3): 991-995. DOI： 10.3969/j.issn.0438-1157.2012.03.045.

摘要

以承钢含钛高炉渣、(NH4)2SO4和KHSO4为主要原料，通过熔融反应法使其中的钛转化为易溶于水的形式，达到回收钛的目的。考察了(NH4)2SO4加入量、KHSO4加入量、加热温度和保温时间对钛回收率的影响。实验结果表明，反应温度和保温时间对钛回收率的影响较大。回收钛的最适条件为：含钛高炉渣与(NH4)2SO4的质量比为1∶6，反应温度为350℃，保温时间为27 min，在此条件下钛的回收率为91.7%，硫酸铵中氮的挥发损失率为81.5%。回收钛后所得残渣主要含有大量硫酸钙、二氧化硅和少量钙钛矿、钙铝黄长石。

Abstract

A melting reaction process was developed to transform the titanium in titanium-bearing blast furnace slag into water-soluble one

such as TiOSO4 by the treatment with ammonium sulfate and potassium bisulfate

to recover titanium. The effects of quantities of ammonium sulfate and potassium bisulfate added

reaction temperature and holding time on the recovery rate of titanium were investigated systemically. The experimental results showed that reaction temperature and holding time have a great impact on the recovery of titanium. The recovery rate of titanium was improved with an increase of reaction temperature and holding time. The optimum conditions of titanium recovery from titanium-bearing blast furnace slag were as follows: the mass ratio of slag to ammonium sulfate 1∶6

reaction temperature 350℃

and holding time 27 min. Under such conditions the recovery rate of titanium was up to 91. 7% and the evaporation loss rate of nitrogen from (NH4)2SO4 was 81.5%. The residue obtained after recovery of titanium was mainly composed of CaSO4·H2O

CaSO4·0.5H2O

SiO2

a small amount of CaTiO3 and Ca2Al2SiO7. This study promises significant economic benefits for smelting enterprise.

关键词

Keywords

references

Views

524

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Recovery of titanium dioxide from titanium-bearing solution by using ammonium as precipitant

Optimization of ultrasonic-assisted extraction of PPS oligomers from PPS industrial waste by response surface methodology

Chloride-enhanced activation of peroxymonosulfate via ferrous iron for degradation of PBTC and simultaneous recovery of phosphorus

Advances in upcycling of post-consumer PET

Mechanism study on mechanochemical solid-phase oxidation recovery of spent LiFePO4 batteries

Related Author

ZHANG Yue

WANG Sijia

XUE Xiangxin

WANG Minghui

XU Haibing

ZHU Yingdan

YAN Chun

LIU Dong

Related Institution

School of Materials and Metallurgy, Northeastern University

Pesticide Research Institute, Shenyang Research Institute of Chemical Industry

College of Chemical Engineering, Zhejiang University of Technology

Zhejiang Provincial Key Laboratory of Robotics and Intelligent Manufacturing Equipment Technology,Ningbo Institute of Material Technology and Engineering, Chinese Academy of Sciences

Institute of Water Ecological Environment, Chinese Research Academy of Environmental Sciences

⁰