Effect of sintering temperature on structures and properties of TiO<sub>2</sub>/stainless steel hollow fiber composite membrane

GAO Jiaming; WANG Ming; MA Xiaohua; XU Zhenliang

doi:10.11949/j.issn.0438-1157.20180756

您当前的位置：

首页 >

文章列表页 >

Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane

更新时间：2025-12-10

- Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane
- CIESC Journal Issue 11, Pages: 4879-4886(2018)
- 作者机构：
  
  化学工程联合国家重点实验室, 华东理工大学化学工程研究所膜科学与工程研发中心,上海,200237
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180756
  CLC： Q028.8
- Online First：05 November 2018，
  
  Published：05 November 2018
- 稿件说明：
移动端阅览
GAO Jiaming, WANG Ming, MA Xiaohua, et al. Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane[J]. CIESC Journal, 2018, (11): 4879-4886. DOI: 10.11949/j.issn.0438-1157.20180756.
DOI：

GAO Jiaming, WANG Ming, MA Xiaohua, et al. Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane[J]. CIESC Journal, 2018, (11): 4879-4886. DOI: 10.11949/j.issn.0438-1157.20180756. DOI：

摘要

不锈钢中空纤维膜基膜孔径大，直接涂覆分离层容易产生表面缺陷。在二氧化钛悬浮液中加入聚乙烯醇作为黏结剂，通过真空辅助抽滤法在不锈钢中空纤维基膜表面形成一层均匀的分离层。通过高温烧结得到了TiO2/不锈钢中空纤维复合膜，考察了烧结温度对于TiO2/不锈钢中空纤维复合膜表面分离层形貌和结构的影响。不同烧结温度时，TiO2/不锈钢中空纤维复合膜的表面形貌有所差异；随着烧结温度的升高，不锈钢复合膜的孔径和纯水通量均先升高再下降。当烧结温度为500℃时，表面涂层均匀，孔径分布集中，水通量较高。最后，以SPT-500膜测试了水包油乳液分离效果，分离效率达到99%以上，且具有良好的抗污染性能。

Abstract

Stainless steel hollow fiber membrane has large pore diameter

and the direct coating of the separation layer is liable to cause surface defects. In this paper

polyvinyl alcohol (PVA) is added to the suspension of titanium dioxide as binder

and a uniform separation layer is formed on the surface of stainless steel hollow fiber membrane by vacuum assisted method. TiO2/stainless steel hollow fiber composite membrane was obtained by sintering at high temperature. The influence of sintering temperature on the morphology and structure of the surface separation layer was studied. The surface morphology of TiO2/stainless steel hollow fiber composite membranes was different at different sintering temperatures. The pore size and pure water flux of the composite membranes increased first and then decreased with the increase of sintering temperature. It was found that the surface coating was uniform

the pore size distribution was narrow and the water flux was higher when the sintering temperature was 500℃. Finally

SPT-500 was used to separate oil-water emulsion. The separation efficiency was over 99% and it has a good anti-fouling performance.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Thermo-oxidative degradation characteristics of TPT backsheet from end-of-life photovoltaic modules

Preparation of biobased polyurethane adhesives for flexible packaging and their water-resistance and thermal stability assessment

Revealing mechanisms of tar formation and char structural evolution during lignin pyrolysis from microscopic perspective

Progress of molten salt-assisted thermochemical high-value conversion of biomass

Characterisation of nitrogenous pollutants in solid wastes associated with waste incineration process using polymer non-catalytic reduction denitrification

Related Author

WANG Shangming

LI Xiaofeng

FANG Qiuyu

WANG Qiang

ZHANG Guoping

CHEN Yunan

CHEN Bin

ZHANG Haisheng

Related Institution

State Key Laboratory of Multiphase Flow in Power Engineering, Xi’an Jiaotong University

School of Chemical Engineering and Light Industry, Guangdong University of Technology

Zhongshan Kingho Chemical Co., Ltd.

State Key Laboratory of Mesoscience and Engineering, Institute of Process Engineering, Chinese Academy of Sciences

Innovation Academy for Green Manufacture, Chinese Academy of Sciences

⁰

Effect of sintering temperature on structures and properties of TiO2/stainless steel hollow fiber composite membrane

DOI：10.11949/j.issn.0438-1157.20180756

摘要

Abstract

关键词

Keywords

references

Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane