Electrochemical performance of Li3VO4 modified Ni-rich LiNi0.8Co0.1Mn0.1O2 cathode materials

SONG Liubin; TANG Fuli; XIAO Zhongliang

doi:10.11949/j.issn.0438-1157.20180664

您当前的位置：

首页 >

文章列表页 >

Electrochemical performance of Li₃VO₄ modified Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials

更新时间：2025-12-10

- Electrochemical performance of Li₃VO₄ modified Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials
- CIESC Journal Issue 12, Pages: 5332-5338(2018)
- 作者机构：
  
  长沙理工大学化学与生物工程学院,湖南,长沙,410114
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180664
  CLC： M912.9
- Online First：05 December 2018，
  
  Published：05 December 2018
- 稿件说明：
移动端阅览
SONG Liubin, TANG Fuli, XIAO Zhongliang. Electrochemical performance of Li₃VO₄ modified Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials[J]. CIESC Journal, 2018, (12): 5332-5338. DOI: 10.11949/j.issn.0438-1157.20180664.
DOI：

SONG Liubin, TANG Fuli, XIAO Zhongliang. Electrochemical performance of Li₃VO₄ modified Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials[J]. CIESC Journal, 2018, (12): 5332-5338. DOI: 10.11949/j.issn.0438-1157.20180664. DOI：

摘要

采用湿法融合技术及高温固相法合成Li3VO4包覆的LiNi0.8Co0.1Mn0.1O2正极材料。通过X射线衍射（XRD）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）等方法研究材料的结晶相、形貌、微观结构。研究表明，Li3VO4均匀地包覆在LiNi0.8Co0.1Mn0.1O2表面，未改变原材料的材料结构和形貌，包覆层厚度为1～2 nm。不同含量的Li3VO4对LiNi0.8Co0.1Mn0.1O2正极材料进行修饰研究表明，3%（质量）Li3VO4包覆的LiNi0.8Co0.1Mn0.1O2在1 C下100次循环后容量保持率为94.13%，具有最佳的倍率性能和循环性能。此外，循环伏安（CV）和交流阻抗（EIS）分析表明，Li3VO4能提高Li+电导率，抑制活性材料与电解液之间的副反应，提高材料的电化学性能。

Abstract

The Li3VO4 coated LiNi0.8Co0.1Mn0.1O2 cathode material was synthesized by wet fusion technology and high temperature solid phase method. The crystalline phase

morphology and microstructure of materials were studied by X-ray diffraction (XRD)

scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that Li3VO4 is evenly coated on the surface of LiNi0.8Co0.1Mn0.1O2 without changing the material structure and morphology of the raw materials. The coating thickness is 1-2 nm. The modification of LiNi0.8Co0.1Mn0.1O2 cathode material with different content of Li3VO4 shows that 3%(mass) Li3VO4 coated LiNi0.8Co0.1Mn0.1O2 has a capacity retention rate of 94.13% after 100 cycles under 1 C

which has the best multiplier performance and cycling performance. In addition

cyclic voltammetry (CV) and alternating current impedance (EIS) analysis show that Li3VO4 can increase Li+ conductivity

inhibit the side-effect between active material and electrolyte

and improve the electrochemical properties of materials.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Composite materials of Li2ZrO3 coated LiNi0.8Co0.1Mn0.1O2 and its electrochemical properties

Optimization for synthesis technology of LiNi0.8Co0.1Mn0.1O2 cathode material and electrochemical performance

Investigation on synthesis conditions of LiNi1-x-yCoxMnyO2 cathode material via co-precipitation

Effects of Cr-doping on structure and electrochemical performance of lithiumand manganese-rich cathode materials Li1.2Ni0.2Mn0.6O2

Synthesis of Li3PO4-doped Li(Ni0.5Co0.2Mn0.3)O2 by rheological phase method and its electrochemical performance as cathode material for Li-ion batteries

Related Author

SONG Liubin

LIU Jiao

XIAO Zhongliang

LI Lingjun

CAO Zhong

HU Chaoming

LI Xinyu

TANG Fuli

Related Institution

Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation, School of Chemistry and Biological Engineering, Changsha University of Science and Technology

College of Materials Science and Engineering, Changsha University of Science and Technology

Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences

Key Laboratory of Green Process and Engineering, Institute of Process Engineering, Chinese Academy of Sciences

College of Materials Science and Engineering, Jiangsu University

⁰