Preparation of fibrous γ-alumina with large pore volume via co-current dropwise addition method

WAN Yanchun; WANG Yujun; LUO Guangsheng

doi:10.11949/j.issn.0438-1157.20180609

您当前的位置：

首页 >

文章列表页 >

Preparation of fibrous γ-alumina with large pore volume via co-current dropwise addition method

更新时间：2025-12-10

- Preparation of fibrous γ-alumina with large pore volume via co-current dropwise addition method
- CIESC Journal Issue 11, Pages: 4840-4847(2018)
- 作者机构：
  
  化学工程联合国家重点实验室, 清华大学化学工程系,北京,100084
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180609
  CLC： Q133.1
- Online First：05 November 2018，
  
  Published：05 November 2018
- 稿件说明：
移动端阅览
WAN Yanchun, WANG Yujun, LUO Guangsheng. Preparation of fibrous γ-alumina with large pore volume via co-current dropwise addition method[J]. CIESC Journal, 2018, (11): 4840-4847.
DOI：

WAN Yanchun, WANG Yujun, LUO Guangsheng. Preparation of fibrous γ-alumina with large pore volume via co-current dropwise addition method[J]. CIESC Journal, 2018, (11): 4840-4847. DOI： 10.11949/j.issn.0438-1157.20180609.

摘要

以偏铝酸钠（NaAlO2）-硫酸铝（Al2（SO4）3）为原料，利用并流滴加法控制沉淀过程的反应pH，并通过调节原料浓度、老化pH和加入表面活性剂十二烷基苯磺酸钠（SDBS）等方法，成功制备得到了大孔容纤维状的γ-氧化铝。实验发现，不同的原料浓度会影响成核-生长过程，得到不规则片状、纤维状或颗粒状等不同形貌的γ-氧化铝，其中纤维状可形成大孔容。当NaAlO2浓度为0.5~0.75 mol/L，反应pH控制在8~9.5，老化pH控制在9左右时，得到的γ-氧化铝呈纤维状，孔容较大；此外，在老化过程中添加SDBS可进一步提高孔容，并改善孔径分布。本方法成功制备出孔容为1.35~2.19 ml/g、比表面积为300~500 m2/g、平均孔径为14~21 nm的纤维状γ-氧化铝，纤维长度为50~60 nm，纤维宽度约5 nm，可为渣油加氢过程提供一种性能良好的催化剂载体。

Abstract

A co-current dropwise addition method was employed to prepare γ-alumina with a large pore volume with sodium aluminate (NaAlO2) and aluminum sulfate (Al2(SO4)3) used as raw materials. The effects of the reaction pH during the precipitation process

raw material concentration

aging pH and adding surfactant sodium dodecyl benzene sulfonate (SDBS) were investigated. It was found that raw material concentration could affect the nucleation-growth process and result in different morphologies

such as irregular sheets

fibers or granules

in which fibers could form the largest pore volume. When the NaAlO2 concentration was 0.5-0.75 mol/L

the reaction pH was controlled at 8-9.5 and the aging pH was controlled at about 9

the obtained γ-alumina is fibrous. Besides

adding SDBS during the aging process could further improve the pore volume and pore size distribution. The method successfully prepared fibrous γ-alumina with a pore volume of 1.35-2.19 ml/g

a specific surface area of 300-500 m2/g and an average pore diameter of 14-21 nm

a fiber length of 50-60 nm and diameter about 5 nm. It can provide a good catalyst carrier for the residue hydrogenation process.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of lignin structure and surfactant on cellulase adsorption by lignin

Research progress of ionic liquids in separation of aromatics/alkanes and olefins/alkanes

Recent advances in machine learning for modeling and control of crystallization processes

Study on entropy wave production and dissipation in partially premixed swirl flames subject to inlet perturbations

Oxygen mass transfer performance of hollow fiber non-bubble aeration membrane based on gas/liquid-phase measurement method

Related Author

姚兰1

Related Institution

1湖北工业大学化学与环境工程学院

山东大学生命科学学院

⁰