Effect of acrylate amount on properties of swelling-block waterborne polyurethane

更新时间：2025-12-10

- Effect of acrylate amount on properties of swelling-block waterborne polyurethane
- CIESC Journal Issue 11, Pages: 4856-4861(2018)
- 作者机构：
  
  1. 化学工程联合国家重点实验室, 浙江大学化学工程与生物工程学院,浙江,杭州,310027
  2. 杭华油墨股份有限公司,浙江,杭州,310018
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180481
  CLC： Q436.5
- Online First：05 November 2018，
  
  Published：05 November 2018
- 稿件说明：
移动端阅览
YANG Dongjie, SHI Yiming, SHAN Guorong. Effect of acrylate amount on properties of swelling-block waterborne polyurethane[J]. CIESC Journal, 2018, (11): 4856-4861.
DOI：

YANG Dongjie, SHI Yiming, SHAN Guorong. Effect of acrylate amount on properties of swelling-block waterborne polyurethane[J]. CIESC Journal, 2018, (11): 4856-4861. DOI： 10.11949/j.issn.0438-1157.20180481.

摘要

以甲基丙烯酸甲酯（MMA）、丙烯酸正丁酯（BA）为单体，通过巯基乙醇链转移自由基无规共聚合成端羟基聚丙烯酸酯（PA-OH），采用嵌段共聚法将PA-OH与水性聚氨酯（WPU）嵌段，通过预聚体分散法制得聚丙烯酸酯嵌段水性聚氨酯乳液（WPUA），进而通过乳液聚合法制备了一系列以MMA/BA为单体的聚丙烯酸酯嵌段-溶胀水性聚氨酯复合乳液（WPUA-PA），结果表明WPUA-PA中丙烯酸酯量最多可达到WPUA的240%，当丙烯酸酯量为WPUA的120%时WPUA-PA的性能最佳，此时乳液平均粒径为68 nm、粒径分布指数为0.174，胶膜拉伸强度为13.88 MPa、断裂伸长率为558.3%、吸水率为4.94%，且具有优异的乳液稳定性。

Abstract

Hydroxyl-terminated polyacrylate (PA-OH) was synthesized by free radical copolymerization of methyl methacrylate (MMA) and n-butyl acrylate (BA) using mercaptoethanol as chain transfer. PA-OH was blocked with waterborne polyurethane (WPU) by block polymerization

and then prepared polyacrylate block waterborne polyurethane emulsion (WPUA) by prepolymer dispersion. A series of polyacrylate swelling-block waterborne polyurethane composite emulsions with MMA/BA as the monomer were prepared by emulsion polymerization. The results showed that the dosage of acrylates in WPUA-PA can reach 240% of WPUA. WPUA-PA has the best performance when the dosage of acrylates is 120% of WPUA. The average emulsion particle size is 68 nm

the particle distribution index is 0.174

the tensile strength of the film is 13.88 MPa

the elongation at break is 558.3%

the water absorption is 4.94%

and the emulsion stability is excellent.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Hydrolysis reaction mechanism of CNCl on the surface of composite metal CuCr2O4

Thermodynamic study of germanium-impurity competitive deposition in GeCl4-MxCly-H2 system

Performance study of gas-liquid vortex separators under low cross-sectional gas velocity

A two-stage dual-channel deep learning model for chemical fault classification

Methods of adaptive prediction and abnormal states traceability for sulphur content in flue gas desulfurization process

Related Author

No data

Related Institution

No data

⁰